Through the powder metallurgy technique, alloys of the eutectic composition of the Zn-Al system were manufactured (22.3 wt.%Al), reinforced with Ag additions (0.5, 1, 2.5, 5 wt.%), with subsequent annealing heat treatment at three different temperatures; 100, 150 and 200°C for 1 hr. X-ray diffraction, optical microscopy and mechanical tests were performed on the resulting samples. The addition of Ag favors the formation of alpha and beta compounds with Al and Zn respectively, which improves the compressive strength of the alloy. However, with the presence of Ag the hardness is decreased. On the other hand, the application of an annealing heat treatment, shows no significant effect on the evaluated properties of the alloy. The microstructure of the alloys resulted in the presence of very small grains smaller than 1 mm and with rounded morphology.

The objective of the present study was to investigate the effects of Sn addition on the mechanical and corrosion properties of Mg-1Zn-1Zr-xSn (x = 1, 2, 3, 4, 5 wt.%) alloys prepared by powder-in-tube rolling (PTR) method. The PTR-treated Mg alloys reached 98.3% of theoretical density. The hardness of the alloy increased with Sn addition. Two main intermetallic phases, Mg2Sn and Zn2Zr3, were formed in the alloys. The Mg2Sn intermetallic particles were observed along the grain boundaries, while the Zn2Zr3 particles were distributed in the Mg matrix. The addition of 1 wt. % Sn caused the corrosion potential to shift toward a more positive value, and the resulting alloy exhibited low corrosion current density.