Concrete-filled steel tube arch bridge is filled with concrete inside the steel tube. The radial constraint of the steel tube limits the expansion of the compression concrete, which makes the concrete in the three-way compression state, thus significantly improving the compressive strength of the concrete. At the same time, it can simplify the construction process and shorten the construction period. Since the rapid development of concretefilled steel tubular tied arch bridge in the 1990s, a large number of such Bridges have suffered from the defects of steel concrete, loose tie rod, and hanger rod rust, etc. Therefore, the reinforcement technology for various diseases has been studied, among which the reinforcement technology for hanger rod replacement is the most complicated and more difficult. As more and more bridges of this type enter the period of reinforcement, it ismore and more urgent to study the reinforcement technology of suspenders. Taking a bridge that has been in service for 23 years as an example, this paper discusses the construction method and construction monitoring of replacing the suspender, so as to guide the construction monitoring of the bridge. Finally, the construction monitoring results of the bridge are given, which can provide reference for the replacement of the suspender of this type of bridge.

With the rapid development of the construction industry and higher requirements on the properties of materials, extensive studies have been made to improve the property of the concrete and cementitious materials. This paper mainly studies the mechanical property, anti-chlorine ion diffusion, anti-chlorine ion diffusion, anti-freezing performance, hydration process, microstructure and rheological property of the concrete and cementitious materials after adding cellulose nanofibers. Results showed that the compressive strength of C40 concrete with 0.15% cellulose nanofibers added was 75.72 MPa at 56 days of age, 23.11% higher than that of the control group. It was also higher than that of concrete with 0.20% cellulose nanofibers admixture added. When the content of cellulose nanofibers was 0.15%, the flexural strength reached the maximum value of 6.55 MPa, improving by 24% compared with the control group. Under the circumstances of 150 freeze-thaw cycles, the mass loss rate of C50 concrete with 0.15% CNFs admixture registered at 0.41%, reducing by 0.81% compared with the control group. However, when the cellulose nanofibers increased to 0.20%, the mass loss rate of the concrete reached 0.48%, indicating that adding an appropriate amount of cellulose nanofibers could improve the performance of the concrete. The study provides a strong scientific basis for modifying concrete and cementitious materials.

L’articolo offre la sintesi di uno studio relativo a una comparazione di un campione di testi italiani, ovvero prodotti da informatori di madrelingua italiana con: 1) da un lato un campione parallelo di produzioni scritte dei parlanti nativi del polacco; 2) dall’altro lato un campione di testi paralleli prodotti in italiano da un gruppo di apprendenti dell’italiano come LS madrelingua polacchi. L’analisi si concentra sulla presenza di sequenze principali e secondarie individuate secondo il modello Quaestio, nonché sull’utilizzo di anafore fedeli e infedeli.