This article proposes these of vibratory machining to Ti-6Al-4V titanium alloy as finishing treatment. Titanium alloy was used in the aerospace industry, military, metallurgical, automotive and medical processes, extreme sports and other. The three-level three-factor Box-Behnken experiment examined the influence of machining time of vibratory machining, the type of mass finishing media used and the initial state of the surface layer on the mass loss, geometric structure of the surface, micro hardness and the optimal process parameters were determined. Considerations were given the surfaces after milling, after cutting with a band saw and after the sanding process. The experiment used three types of mass finishing media: polyester, porcelain and metal. Duration of vibratory machining treatment was assumed to be 20, 40, 60 minutes. The form profiles before and after vibratory machining were determined with the Talysurf CCI Lite - Taylor Hobson optical profiler. Future tests should concern research to carry out tests using abrasive pastes with a larger granulation of abrasive grains, to carry out tests for longer processing times and to determine the time after which the parameters of geometrical structure of the surface change is unnoticeable.

The effect of CaSiAl modification (43-49% Ca, 43-48% Si, 2% Al) on the non-metallic inclusions and mechanical properties of cast lowcarbon steel is discussed. Tests were carried out on the cast steel with 0.2% C and micro-additives of V and Nb, used mainly for heavy steel castings (e.g. slag ladles). The modifier in an amount of 1.5 and 3 kg / Mg was introduced to the liquid steel before tapping the metal into a ladle. Test ingots of Y type and a weight of 10 kg were cast and then subjected to a normalizing heat treatment. Using light microscopy and scanning electron microscopy, qualitative and quantitative evaluation of the non-metallic inclusions present in as-cast samples was carried out. Additionally, tests of mechanical strength and impact strength were performed on cast steel with and without the different content of modifier. It was found that increasing the modifier addition affected impact strength but had no significant effect on tensile strength and yield strength. The material with high impact strength had the smallest area fraction of non-metallic inclusions in the microstructure (0.20%). The introduction of modifiers changed the morphology of non-metallic inclusions from dendritic to regular and nodular shapes.