The article reports the results of research on the influence of the alternate intermittent deformation of specimens by a torsion method on the Bauschinger effect in the Zr-1%Nb zirconium-based alloy. Tests were carried out using an STD 812 torsion plastometer. Based on the tests carried out, diagrams have been plotted, which represent the influence of the pre-deformation magnitude, the temperature of heat treatment prior to deformation, and deformation rate on the variation in the values of the flow stress and yield strength of the alloy under study. Conditions have been defined, in which larger magnitudes of plastic deformation of Zr-1Nb% alloy material can be used during its cold plastic working.
The study proposed the model of “guide mark” defects formation on the internal surface of pipes, produced on PRM mills of PRP – 140. The research of pipe forming at plug rolling mill with stub mandrel has been carried out; regularities of the dimensionless parameters characterizing the deformation of the gap release, depending on the reduction ratio, were determined. The model of “guide mark” defect formation on the internal surface of the pipe has been proposed. This allows for lesser wall thickness variation of rough tubes. It has been shown that, when using dioctahedral pass designs in comparison with hexagonal pass designs the proportion of displaced volume along the pipe axis is greater but the value is lower; thereby, the risk of “guide mark” defect forming is reduced.