This study was carried out to evaluate the aspect of microstructure and mechanical property development on additive manufactured pure Ti at elevated heat-input. For this work, pure Ti powder (commercial purity, grade 1) was selected, and selective laser melting was conducted from 0.5 to 1.4 J/mm. As a result, increase in heat-input led to the significant grain growth form 4 μm to 12 μm, accompanying with the change of grain shape, correctly widmanstätten structured grains. In addition, Vickers microhardness was notably increased from 228 Hv to 358 Hv in accordance with elevated heat-input, which was attributed to the increased concentration of oxygen and nitrogen mainly occurred during selected laser melting process.