This paper presents the results of research of Ni/diamond composite coatings produced by electrochemical reduction method. Research was focused on composite coatings with nickel matrix and diamond as a disperse phase and for comparison purposes on nanocrystalline nickel coatings. Ni/diamond composite coatings were produced in baths with different content of nanodiamond powder. The structures of the dispersed phase and the composite coatings were analysed by using X-ray diffraction, scanning electron microscopy and light microscopy. Measurements of selected properties of the coatings were performed, including roughness, microhardness, adhesion and abrasive wear resistance. The research results indicate that the produced coatings have a compact structure and good adherence to steel substrate. Moreover, nanocrystalline Ni/diamond composite coatings exhibit greater hardness and reduced abrasive wear resistance compared to nanocrystalline nickel coatings.
The paper presents the results of the electrodeposition of nickel composite coatings reinforced with the ceramic SiC particles. A Watts type galvanic bath modified with various organic additives was used. These additives were: 2-sulfobenzoic acid imide (LSA), dioctyl sulfosuccinate sodium salt (DSS), sodium dodecyl sulfate (SDS), tris (hydroxymethyl) aminomethane (THAM) and hexamethyldisilizane (HMDS). The nickel composite coating was electrodeposited on a 2xxx aluminum alloy series substrate (EN-AW 2017) with zinc interlayer. Studies concerned the effect of the applied organic additives on properties of composite coatings such as: microstructure, microhardness, adhesion to the substrate, corrosion resistance and roughness. The structure of the coatings was assessed by scanning electron microscopy and light microscopy. Based on the studies of zeta potential it was found that the bath modification had a significant impact on the amount of the ceramic phase embedded in metal matrix. The tests conducted in a model 0.01 M KCl solution were not fully representative of the true behavior of particles in a Watts bath.
The present work concerns analysis of the possibilities of synthesis of Ni-TiO2 composite coatings from electrolytes containing formate nickel complexes. A magnetic field was applied as an additional factor enabling modification of properties of the synthesized coatings through its influence on electrode processes. The presented data describes the effect of electrode potential, TiO2 concentration in the electrolyte as well as the value of the magnetic field induction vector on the deposition rate, composition, current efficiency, structure, surface states and morphology of synthesized coatings. The studies were preceded by thermodynamic analysis of the electrolyte. The obtained results indicated possibilities of synthesis of composites containing up to 0.97 wt. % of TiO2. Depending on applied electrolysis conditions current efficiency amounted to from 61.2 to 75.1%.
The microstructure and macroscopic properties of WC-50Ni+stellite 1(Co-Cr-W, ST1) coating layer fabricated by HVOF spray have been investigated. WC-50Ni powder and ST1 powders were mixed in the ratio of 1:0 and 5:5 wt.%, respectively. Argon heat treatment (Ar) and high-frequency heat treatment (H.F.) were conducted on the coating materials. WC was decomposed in the Ar heat treatment specimen, but decomposition of WC was not observed in the H.F. heat treatment specimen. Hardness was measured for as-sprayed WC-50Ni (821.5Hv) and as-sprayed WC-50Ni+ST1 (668.1 Hv). Hardness of Ar heat treatment specimen was reduced by about 14~18% than that of the as-sprayed coating layers. However, when the H.F. heat treatment was performed, the hardness inversely increased by about 6~10% than the as-sprayed coating layer. Based on these results, the method to improve the mechanical property of HVOF sprayed WC-50Ni+ST1 coating layer has also been also discussed.
The paper presents the results of the electrodeposition of nickel composite coatings reinforced with the nano size SiC ceramic particles. The type and size of the ceramic particles or organic additives used play a important role during electrodeposition processes. A Watts type galvanic bath with various organic additives was used. These additives were: 2-sulfobenzoic acid imide, dioctyl sulfosuccinate sodium salt (DSS), sodium dodecyl sulfate, tris (hydroxymethyl) aminomethane and hexamethyldisilizane. The nickel composite coating was electrodeposited on a 2xxx aluminum alloy series substrate (EN-AW 2017) with zinc interlayer. The work concerns the determination of the impact of the change in the zeta potential of SiC nanoceramic particles used on properties of composite coatings (wear resistance, corrosion, etc.). The paper characterized the composite nickel coatings on aluminum alloy using SEM techniques, wear resistance tests by TABER method and coating adhesion to the substrate using the “scratch test” method. The corrosion resistance of coatings was also tested using electrochemical methods. The research allowed to determine the effect of SiC nanoceramic particle size on the value of the zeta potential in the model KCl solution.
The results of research on preparations of alloy Ni-B/B composite coatings produced by chemical reduction method on a carbon steel substrate are collected in this paper. The alloy Ni-B coatings were also investigated for comparative purposes. The produced coatings were subjected to a heat treatment process. The boron powder with the particles size below 1 µm was used as the dispersion phase. The structure of the coatings was examined by X-ray diffraction method. Boron powder particles as well as surface morphology and topography were characterized by scanning electron microscopy. The roughness test, microhardness and corrosion resistance by potentiodynamic method and surface wettability tests were carried out. Analysis of the chemical composition by the EDS method showed that the boron powder particles were evenly embedded in the entire volume of the coating. Ni-B/B composite coatings are characterized by higher hardness than alloy Ni-B coatings. As a result of heat treatment, the Ni3B phase crystallized, which increased the hardness of the coating material. The incorporation of boron powder particles and heat treatment reduce the corrosion resistance of coatings. All produced coatings exhibited hydrophobic properties.