In this study, we investigated the effect of cladding on structural carbon steel (S45C) using 5%Cr-1.5%Mo-Fe powder (SKD61), which is expected to show economically efficient production of die-casting parts. The process conditions were performed under argon atmosphere using a diode laser source with specialized wavelength of 900-1070 nm, and the output conditions were 3, 4, and 5 kW, respectively. After the cladding was completed, the surface coating layer’s shape and the microstructure were analyzed. The hardness test was carried out with Micro Vickers hardness tester under 500 gram-force along the normal line at the interval of 0.2 mm from the surface to core direction on the cross-sectional area. In addition, polarization curve test of the surface coating layer was performed to investigate the corrosion resistance characteristics.

The properties of expansive concretes made of two types of cement: Portland cement CEM I and blast furnace slag cement CEM III were tested. The expansion of the concrete was caused by using an expansive admixture containing aluminium powder added in an amount of 0.5; 1 and 1.5% of cement mass. It was found that the compressive strength of concrete with CEM I decreased after using an expansive admixture in the amount of more than 0.5% of the cement mass. The compressive strength of concrete with CEM III decrease after addition of admixture in the entire range of dosages used. On the basis of electrochemical measurements, it was found no influence of an expansive admixture on corrosion of reinforcing steel. The use of an expansive admixture causes a slight increase in the effective diffusion coefficient of chloride ions in concrete.