@ARTICLE{Zhang_Li_Enhanced_2024,
 author={Zhang, Li and Li, Nan},
 volume={vol. 69},
 number={No 4},
 pages={1473-1480},
 journal={Archives of Metallurgy and Materials},
 howpublished={online},
 year={2024},
 publisher={Institute of Metallurgy and Materials Science of Polish Academy of Sciences},
 publisher={Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences},
 abstract={The microstructure evolution, texture and tensile properties of the Mg-8Li dual-phase alloys processed by hot-extrusion and friction stir processing were investigated. It was found that the friction stir processing was more advantageous when compared with hot-extrusion in achieving the superior mechanical properties. The tensile strength, yield strength and elongation of the as-FSPed alloy reached 235.4 MPa, 185.3 MPa and 35.6%, respectively. The outstanding strength-ductility combination of the ­as-FSPed Mg-8Li alloy was ascribed to refined grains, weakened texture and formation of high-fraction high angle grain boundaries.},
 title={Enhanced Mechanical Properties of Mg-8Li Dual-Phase Alloy Processed by Friction Stirring Versus Hot-Extrusion},
 type={Article},
 URL={http://czasopisma.pan.pl/Content/133542/AMM-2024-4-27-Li%20Zhang.pdf},
 doi={10.24425/amm.2024.151417},
 keywords={Microstructure, mechanical property, Mg-8%Li alloy, hot-extrusion, friction stir processing},
}