The presented access the influence of Mn content (0-0.94 wt.%) on the course of the cooling curves, phase transformation, macrostructure, and microstructure of Al-Cu alloys for three series: initial (Series I), with the addition of an AlTi master (Series II), and modified with AlTi5B1 (Series III). The maximum degree of undercooling ΔT was determined based on the cooling curves. The surface density of the grains (NA) was determined and associated with the inverse of solidification interval 1/ΔTk. Titanium (contained in the charge materials as well as the modifier) has a significant effect on the grinding of the primary grains in the tested alloys. A DSC thermal analysis allowed for the determination of phase transition temperatures under conditions close to equilibrium. For series II and III, the number of grains decreases above 0.2 wt.% Mn with a simultaneous increase in solidification interval 1/ΔTk. The presence of Al2Cu eutectics as well as the Cu-, Fe-, and Mn-containing phases in the examined samples was demonstrated using scanning electron microscopy.
This paper presents results of experimental research concerning the impact of an innovative method of micro-jet cooling on the padding
weld performed with MIG welding. Micro-jet cooling is a novel method patented in 2011. It enables to steer the parameters of weld
cooling in a precise manner. In addition, various elements which may e.g. enhance hardness or alter tribological properties can be entered
into its top surface, depending on the applied cooling gas. The material under study was steel 20MnCr5, which was subject to the welding
process with micro-jet cooling and without cooling. Nitrogen was used as a cooling gas. The main parameter of weld assessment was wear
intensity. The tests were conducted in a tribological pin-on-disc type position. The following results exhibit growth at approximately 5% in
wear resistance of padding welds with micro-jet cooling.
In this paper, the influence of Mo addition on the structure and mechanical properties of the NiCoMnIn alloys have been studied. Series of polycrystalline NiCoMnIn alloys containing from 0 to 5 mas.% of Mo were produced by the arc melting technique. For the alloys containing Mo, two-phase microstructure was observed. Mo-rich precipitates were distributed randomly in the matrix. The relative volume fraction of the precipitates depends on the Mo content. The numbers of the Mo rich precipitates increases with the Mo contents. The structures of the phases were determined by the TEM. The mechanical properties of the alloys are strongly affected by Mo addition contents. Brittleness of the alloys increases with the Mo contents.
The effects of Mg and Ca on sulfide modification of sulphur steel were studied to elucidate the difference between micromagnesium treatment and micro-calcium treatment for the inclusion of sulphur steel. The results show that the inclusions in the steel appeared with an oxide core of Al2O3 and MnS wrapped. After the addition of Mg, the core was changed to spinel, and the MnS coating was changed to Mn-Mg-S. After Ca was added, the core was changed to Ca-Al-O, and the MnS coating was changed to Mn-Ca-S. The Mg content was higher than Ca content in the sulfides of the steel. Therefore, Mg was more effective than Ca in terms of sulfide modification with the same content of Mg and Ca in steel, but the yielding rate of Mg was lower than that of Ca. The Mg content in the oxide core was higher than Mg of the coating of the inclusions in the steel treated with Mg or Mg-Ca. In contrast, the Ca content in the oxide core was lower than Ca of the coating of the inclusions in the steel treated with Ca or Mg-Ca. MnS formed and precipitated during the melt solidification process. The complex sulfide (Mg-Mn-S) was precipitated around MgO·Al2O3 in the Mg treated steel during the cooling process. CaS inclusion was precipitated on the CaO·Al2O3 inclusions in the liquid Ca-treated steel. Thus, CaS was formed first, whereas MnS was formed during the cooling process, followed by the formation of complex sulfide (CaS+MnS), which finally precipitated around CaO·Al2O3 in the Ca-treated steel.
The work deal with an assembling and comparing of transformation diagrams of two low-alloy steels, specifically 16MnCrS5 and 20MnCrS5. In this work, diagrams of the type of CCT and DCCT of both steels were assembled. Transformation diagrams were assembled on the basis of dilatometric tests realized on the plastometer Gleeble 3800, of metallographic analyses and of hardness measurements. In addition, for comparison, the transformation diagrams were assembled even with use of the QTSteel 3.2 software. Uniform austenitization temperature of 850°C was chosen in case of both steels and even both types of diagrams. In case of both steels, an influence of deformation led to expected acceleration of phase transformations controlled by diffusion and also of bainite transformation. In both cases, the kinetics of martensitic transformation was not significantly affected by deformation.
The paper presents the results of study on heavy metals in needles of Pinus sylvestris in selected pine forests in Słowiński National Park. It was evidenced that heavy metal contents (Zn, Cu, Mn and Fe) in needles of Pinus sylvestris varied depending on the metal, the age of the needles and the humidity of a forest complex. Variation coefficients of such metals remained at the level of: 13-30% (Zn), 3-6% (Cu), 13-34% (Mn) and 12-30% (Fe) depending on the age of the needles. In the case of Zn, Mn and Fe higher concentrations of researched metal were found in the 2-year-old needles than in 1 year old needles, and in the case of Cu in 1 year old needles than in 2-year-old needles. The increase of zinc concentration found in 1-year-old needles after rainfall sums was (Bw, r = 0.67, p < 0.05, n = 24) and (Bśw, r = 0.39, p < 0.05, n = 24) in 2-year-old needles. The content of the above mentioned metals in needles of dry coniferous forests (Bs), fresh coniferous forests (Bśw) and humid coniferous forests (Bw) of the ground cover constitute the following decreasing series: Mn(323.8) > Fe(103.4) > Zn(65.5) > Cu(5.9).
The paper presents influence of soaking parameters (temperature and time) on structure and mechanical properties of spheroidal graphite
nickel-manganese-copper cast iron, containing: 7.2% Ni, 2.6% Mn and 2.4% Cu. Raw castings showed austenitic structure and relatively
low hardness (150 HBW) guaranteeing their good machinability. Heat treatment consisted in soaking the castings within 400 to 600°C for
2 to 10 hours followed by air-cooling. In most cases, soaking caused changes in structure and, in consequence, an increase of hardness in
comparison to raw castings. The highest hardness and tensile strength was obtained after soaking at 550°C for 6 hours. At the same time,
decrease of the parameters related to plasticity of cast iron (elongation and impact strength) was observed. This resulted from the fact that,
in these conditions, the largest fraction of fine-acicular ferrite with relatively high hardness (490 HV0.1) was created in the matrix. At
lower temperatures and after shorter soaking times, hardness and tensile strength were lower because of smaller degree of austenite
transformation. At higher temperatures and after longer soaking times, fine-dispersive ferrite was produced. That resulted in slightly lower
material hardness.
Presence of iron in Al-Si cast alloys is common problem mainly in secondary (recycled) aluminium alloys. Better understanding of iron
influence in this kind of alloys can lead to reduction of final castings cost. Presented article deals with examination of detrimental iron
effect in AlSi10MgMn cast alloy. Microstructural analysis and ultimate tensile strength testing were used to consider influence of iron to
microstructure and mechanical properties of selected alloy
The gas-tungsten arc (GTA) welding behaviors of a magnesium matrix composite reinforced with SiC particles were examined in terms of
microstructure characteristics and process efficiencies. This study focused on the effects of the GTAW process parameters (like welding
current in the range of 100/200 A) on the size of the fusion zone (FZ). The analyses revealed the strong influence of the GTA welding
process on the width and depth of the fusion zone and also on the refinement of the microstructure in the fusion zone. Additionally, the
results of dendrite arm size (DAS) measurements were presented.
Determined were direction and intensity of influence of alloying additions on the number of eutectic graphite colonies in austenitic cast iron Ni-Mn-Cu. Chemical composition of the cast iron was 1.7 to 3.3% C, 1.4 to 3.1% Si, 2.8 to 9.9% Ni, 0.4 to 7.7% Mn, 0 to 4.6% Cu, 0.14 to 0.16% P and 0.03 to 0.04% S. Analysed were structures of mottled (20 castings) and grey (20 castings) cast iron. Obtained were regression equations determining influence intensity of individual components on the number of graphite colonies per 1 cm2 (LK). It was found that, in spite of high total content of alloying elements in the examined cast iron, the element that mainly decides the LK value is carbon, like in a plain cast iron.
In the paper, a relationship between chemical composition of Ni-Mn-Cu cast iron and its structure, hardness and corrosion resistance is
determined. The examinations showed a decrease of thermodynamic stability of austenite together with decreasing nickel equivalent value,
in cast iron solidifying according to both the stable and the metastable systems. As a result of increasing degree of austenite
transformation, the created martensite caused a significant hardness increase, accompanied by small decline of corrosion resistance. It was
found at the same time that solidification way of the alloy and its matrix structure affect corrosion resista
Within the presented work, the effect of austenite transformation on abrasive wear as well as on rate and nature of corrosive destruction
of spheroidal Ni-Mn-Cu cast iron was determined. Cast iron contained: 3.1÷3.4 %C, 2.1÷2.3 %Si, 2.3÷3.3 %Mn, 2.3÷2.5 %Cu and
4.8÷9.3 %Ni. At a higher degree of austenite transformation in the alloys with nickel equivalent below 16.0%, abrasive wear resistance
was significantly higher. Examinations of the corrosion resistance were carried out with the use of gravimetric and potentiodynamic
method. It was shown that higher degree of austenite transformation results in significantly higher abrasive wear resistance and slightly
higher corrosion rate, as determined by the gravimetric method. However, results of potentiodynamic examinations showed creation
of a smaller number of deep pinholes, which is a favourable phenomenon from the viewpoint of corrosion resistance.
We investigated the antioxidant defense mechanism, metal uptake and lipid peroxidation (LPO) levels at different leaf positions in Mentha piperita L. grown in Mn2+-deficient and control conditions. Under manganese deficiency the activity of superoxide dismutase (SOD), catalase (CAT) and guaiacol peroxidase (GuaPOX) and the content of ascorbate, chlorophyll, and carotenoid under Mn2+ deficiency were significantly lower than in the control for all leaf positions. SOD activity correlated positively with Mn2+ uptake. Fe2+ uptake was inhibited by Mn2+ deficiency. During early stages of Mn2+ deficiency, M. piperita leaves showed relatively more antioxidant activity and lower LPO. Towards the final stages of the treatment period, comparatively lower SOD, CAT and GuaPOX activity and higher LPO levels accelerated the senescence process.
In this work, vacuum hot pressed Ni-Mn-Sn-In Heusler alloys with different concentration of In (0, 2 and 4 at.%), were investigated. The magneto-structural behaviour and microstructure dependencies on chemical composition and on heat treatment were examined. It was found that the martensite start transformation temperature increases with growing In content and to a lesser extent with increasing temperature of heat treatment. The high energy X-ray synchrotron radiation results, demonstrated that both chemical composition as well as temperature of heat treatment slightly modified the crystal structures of the studied alloys. Microstructural investigation performed by transmission electron microscopy confirmed chemical composition and crystal structure changes in the alloys.
Influence of the initial grain size on hot deformation behavior of the low-alloy Mn-Ti-B steel was investigated. The uniaxial compression tests were performed in range of the deformation temperatures of 900-1200°C and strain rates of 0.1-10 s–1. One set of samples was heated directly to the deformation temperature, which corresponded to the initial austenitic grain size of 19-56 μm; the other set of samples was uniformly preheated at the temperature of 1200°C. Whereas the values of activation energy, peak stress and steady-state stress values practically did not depend on the initial austenitic grain size, the peak strain values of coarser-grained structure significantly increase mainly at high values of the Zener-Hollomon parameter. This confirms the negative effect of the large size of the initial grain on the dynamic recrystallization kinetics, which can be explained by the reduction in nucleation density.