Archives of Foundry Engineering | 2021 | vo. 21 | No 1

Download PDF Download RIS Download Bibtex

Abstract

Porosity is one of the major problems in casting operations and there are several discussions in the literature about the porosity formation in aluminum castings. Bifilms are the defects that are introduced into the melt by turbulence. They can be detected with reduced pressure test and presented numerically by measuring bifilm index. The measure of bifilm index is the sum of total oxide length given in millimeters from the cross-section of reduced pressure test sample solidified under 0.01 MPa. In this work, low pressure die casting (LPDC) unit was built in an attempt to enhance the producibility rate. The unit consists of a pump housing that was placed inside the melt in the melting furnace where the pressure was applied instead of the whole melt surface. It was observed that the melt quality of A356 alloy was deteriorated over time which had led to higher porosity. This was attributed to the increased oxide thickness of the bifilm by the consumption of air in between the folded oxides. A relationship was found between bifilm index and pore formation.
Go to article

Bibliography

[1] Campbell, J. (2011). Complete Casting Handbook: Metal Casting Processes. Techniques and Design. Elsevier Science.
[2] Bonollo, F., Urban, J., Bonatto, B. & Botter, M. (2005). Gravity and low pressure die casting of aluminium alloys: a technical and economical benchmark. La Metallurgia Italiana. 6, 23-32.
[3] Dispinar, D. & J. Campbell, (2004). Critical assessment of reduced pressure test. Part 2: Quantification. International Journal of Cast Metals Research. 17(5), 287-294.
[4] Raiszadeh, R., & Griffiths, W.D. (2006). A method to study the history of a double oxide film defect in liquid aluminum alloys. Metallurgical and Materials Transactions B. 37(6), 865-871.
[5] Raiszadeh, R., & Griffiths, W.D. (2008). A semi-empirical mathematical model to estimate the duration of the atmosphere within a double oxide film defect in pure aluminum alloy. Metallurgical and Materials Transactions B. 39(2), 298-303.
[6] Raiszadeh, R., & Griffiths, W.D. (2011). The effect of holding liquid aluminum alloys on oxide film content. Metallurgical and Materials Transactions B. 42(1), 133-143.
[7] Aryafar, M., Raiszadeh, R., & Shalbafzadeh, A. (2010). Healing of double oxide film defects in A356 aluminium melt. Journal of materials science. 45(11), 3041-3051.
[8] Farhoodi, B., Raiszadeh, R., & Ghanaatian, M. H. (2014). Role of double oxide film defects in the formation of gas porosity in commercial purity and Sr-containing Al alloys. Journal of Materials Science & Technology. 30(2), 154-162.
[9] Amirinejhad, S., Raiszadeh, R., & Doostmohammadi, H. (2013). Study of double oxide film defect behaviour in liquid Al–Mg alloys. International Journal of Cast Metals Research. 26(6), 330-338.
[10] Bakhtiarani, F.N., & Raiszadeh, R. (2011). Healing of double-oxide film defects in commercial purity aluminum melt. Metallurgical and Materials Transactions B. 42(2), 331-340.
[11] Bagherpour-Torghabeh, H., Raiszadeh, R., & Doostmohammadi, H. (2017). Role of Mechanical Stirring of Al-Mg Melt in the Healing of Bifilm Defect. Metallurgical and Materials Transactions B. 48(6), 3174-3184.
[12] Nateghian, M., Raiszadeh, R., & Doostmohammadi, H. (2012). Behavior of Double-Oxide Film Defects in Al-0.05 wt pct Sr Alloy. Metallurgical and Materials Transactions B. 43(6), 1540-1549.
[13] Stefanescu, D.M. (2005). Computer simulation of shrinkage related defects in metal castings - a review. International Journal of Cast Metals Research. 18, 129-143.
[14] Zhu, J.D., Cockcroft, S.L., Maijer, D.M. & Ding, R. (2005). Simulation of microporosity in A356 aluminium alloy castings. International Journal of Cast Metals Research. 18, 229-235.
[15] Merlin, M., Timelli, G., Bonollo, F. & Garagnani, G.L. (2009). Impact behaviour of A356 alloy for low-pressure die casting automotive wheels. Journal of Materials Processing Technology. 209(2), 1060-1073.
[16] Zhang, B., Maijer, D.M. & Cockcroft, S.L. (2007). Development of a 3-D thermal model of the low-pressure die-cast (LPDC) process of A356 aluminum alloy wheels. Materials Science and Engineering: A, 464(1-2), 295-305.
[17] Zhang, B., Cockcroft, S.L., Maijer, D.M., Zhu, J.D. & Phillion, A.B. Casting defects in low-pressure die-cast aluminum alloy wheels. JOM Journal of the Minerals, Metals and Materials Society, 57(11), 36-43.
[18] Campbell, J. (1968). Hydrostatic tensions in solidifying materials. Transactions of the Metallurgical Society of AIME, 242 (February), 264-267.
[19] Campbell, J. (1968). Hydrostatic tensions in solidifying alloys. Transactions of the Metallurgical Society of AIME, 242 (February), 268-271.
[20] Campbell, J. (1967), Shrinkage pressure in castings (The solidification of a Metal Sphere). Transactions of the Metallurgical Society of AIME, 239 (February), 138-142.
[21] Dispinar, D. & Campbell, J. (2004). Critical assessment of reduced pressure test. Part 1: Porosity phenomena. International Journal of Cast Metals Research. 17(5), 280-286.
[22] Dispinar, D., Akhtar, S., Nordmark, A., Di Sabatino, M., & Arnberg, L. (2010). Degassing, hydrogen and porosity phenomena in A356. Materials Science and Engineering: A. 527(16-17), 3719-3725.
[23] Puga, H., Barbosa, J., Azevedo, T., Ribeiro, S. & Alves, J.L. (2016). Low pressure sand casting of ultrasonically degassed AlSi7Mg0. 3 alloy: Modelling and experimental validation of mould filling. Materials & Design. 94, 384-391.
[24] El-Sayed, M.A. & Essa, K. (2018). Effect of mould type and solidification time on bifilm defects and mechanical properties of Al–7si–0.3 mg alloy castings. Computational and Experimental Studies, 23.
[25] Gyarmati, G., Fegyverneki, G., Mende, T. & Tokár, M. (2019). Characterization of the double oxide film content of liquid aluminum alloys by computed tomography. Materials Characterization. 157, 109925. [26] Gyarmati, G., Fegyverneki, G., Tokár, M., & Mende, T. (2020). The Effects of Rotary Degassing Treatments on the Melt Quality of an Al–Si Casting Alloy. International Journal of Metalcasting. 1-11.
[27] Tiryakioğlu, M. (2020). The Effect of Hydrogen on Pore Formation in Aluminum Alloy Castings: Myth Versus Reality. Metals. 10(3), 368.
[28] Tiryakioğlu, M. (2019). Solubility of hydrogen in liquid aluminium: reanalysis of available data. International Journal of Cast Metals Research. 32(5-6), 315-318.
[29] Tiryakioğlu, M. (2020). A simple model to estimate hydrogen solubility in liquid aluminium alloys. International Journal of Cast Metals Research. 1-3.
Go to article

Authors and Affiliations

O. Gursoy
1
A. Nordmak
2
F. Syvertsen
2
M. Colak
3
K. Tur
4
D. Dispinar
5
ORCID: ORCID

  1. University of Padova, Italy
  2. SINTEF, Norway
  3. University of Bayburt, Turkey
  4. Atilim University, Turkey
  5. Istanbul Technical University, Turkey
Download PDF Download RIS Download Bibtex

Abstract

Titanium alloys belonging to the group of modern metallic materials used in many industries, including the aerospace industries. Induction crucible vacuum furnaces and induction furnaces with cold crucible are most commonly used for their smelting. When operating these devices, one can deal with an adverse phenomenon of decrease in the content of alloy elements that are characterized by higher equilibrium vapour pressure than the matrix metal or titanium, in the metal bath. In the paper, results of the study on aluminium evaporation from the Ti-Al-Nb, Ti-Al-V and Ti-Al alloys (max 6.2 % wt.) during smelting in a vacuum induction melting (VIM) furnace are presented. The experiments were performed at 10 to 1000 Pa for 1973 K and 2023 K. A significant degree of aluminium loss has been demonstrated during the analysed process. The values of relative aluminium loss for all the alloys ranged from 4 % to 25 %. Lowering the pressure in the melting system from 1000 Pa to 10 Pa resulted in increased values of aluminium evaporation flux from 4.82⋅10-5 to 0.000327 g⋅cm-2⋅s-1 for 1973 K and from 9.28⋅10-5 to 0.000344 g⋅cm-2⋅s-1 for 2023 K. The analysis of the results obtained took into account the value of the actual surface of the liquid metal. In the case of melting metals in an induction furnace, this surface depends on the value of power emitted in the charge. At greater power, we observe a significant increase in the bath surface due to the formation of a meniscus.
Go to article

Bibliography

[1] Kostov, A. & Friedrich, B. (2005). Selection of crucible oxides in molten titanium and titanium aluminium alloys by thermo-chemistry calculation. Journal of Mining and Metallurgy. 41B, 113-125. DOI: 10.2298/JMMB0501113K.
[2] Kuang, J.P., Harding, R.A. & Campbell, J. (2000). Investigation into refractories as crucible and mould materials for melting and casting gamma-TiAl alloys. Materials Science and Technology. 16, 1007-1016. DOI: 10.1179/026708300101508964.
[3] Tetsui, T., Kobayashi, T., Mori, T., Kishimoto, T. & Harada, H. (2010). Evaluation of yttrium applicability as a crucible for induction melting of TiAl alloy. Materials Transactions. 51, 1656-1662. DOI: 10.2320/matertrans.MAW20100.
[4] Myszka, D., Karwiński, A., Leśniewski, W. & Wieliczko, P. (2007). Influence of the type of ceramic moulding materials on the top layer of titanium precision castings. Archives of Foundry Engineering. 7(1), 153-156. DOI: 10.7356/ iod.2015.24.
[5] Szkliniarz, A. & Szkliniarz, W. (2011). Assessment quality of Ti alloys melted in induction furnace with ceramic crucible. Solid State Phenomena. 176, 139-148. DOI: 10.4028/www.scientific.net/SSP.176.139.
[6] Jinjie, G., Jun, J., Yuan, S.L., Guizhong, L., Yanqing, S. & Hongsheng, D. (2000). Evaporation behavior of aluminum during the cold crucible induction skull melting of titanium aluminum alloys. Metallurgical and Materials Transactions B. 31B, 837-844. DOI: 10.1007/s11663-000-0120-1.
[7] Isawa, T., Nakamura, H. & Murakami, K. (1992). Aluminum evaporation from titanium alloys in EB hearth melting. ISIJ International. 32, 607-615.
[8] Ivanchenko, V., Ivasishin, G. & Semiatin, S. (2003). Evaluation of evaporation losses during electron-beam melting of Ti-Al-V alloys. Metallurgical and Materials Transactions B. 34B, 911-915. DOI: 10.1007/s11663-003-0097-7.
[9] Su, Y., Guo, J., Jia, J., Liu, G. & Liu, Y. (2002). Composition control of a TiAl melt during the induction skull melting (ISM) process. Journal of Alloys and Compounds. 334, 261-266. DOI: 10.1016/S0925-8388(01)01766-2.
[10] Guo, J., Liu, G., Su, Y., Ding, H., Jia, J. & Fu, H. (2002). The critical pressure and impeding pressure of Al evaporation during induction skull melting processing of TiAl. Metallurgical and Materials Transactions A. 31A, 3249-3253. DOI: 10.1007/s11661-002-0311-2.
[11] Gou, J., Liu, Y., Su, Y., Ding, H., Liu, G. & Jia, J. (2000). Evaporation behaviour of aluminum during the cold crucible induction skull melting of titanium aluminum alloys. Metallurgical and Materials Transactions B. 31B, 837-844. DOI: 10.1007/s11663-000-0120-1.
[12] HSC Chemistry ver. 6.1. Outocumpu Research Oy, Pori.
[13] Semiatin, S., Ivanchenko, V., Akhonin, S.O. & Ivasishin, O.M. (2004). Diffusion models for evaporation losses during electron-beam melting of alpha/beta-titanium alloys. Metallurgical and Materials Transactions B. 35B, 235-245. DOI: 10.1007/s11663-004-0025-5.
[14] Song, J.H., Min, B.T., Kim, J. H., Kim, H.W., Hong, S.W. & Chung, S.H. (2005). An electromagnetic and thermal analysis of a cold crucible melting. International Communications in Heat and Mass Transfer. 32, 1325-1336. DOI: 10.1016/j.icheatmasstransfer.2005.07.015.
[15] Zhu, Y., Yang, Y.Q. & Sun, J. (2004). Calculation of activity coefficients for components in ternary Ti alloys and intermetallics as matrix of composites. Transactions of Nonferrous Metals Society of China. 14, 875-879.
[16] Belyanchikov, L.N. (2010). Thermodynamics of Titanium-Based Melts: I. Thermodynamics of the Dissolution of Elements in Liquid Titanium. Russian Metallurgy. 6, 565-567. DOI: 10.1134/S0036029510060194.
[17] Blacha, L. & Labaj, J. (2012). Factors determining the rate of the process of metal bath components. Metalurgija. 51, 529-533.
[18] Ward, R.G. (1963). Evaporative losses during vacuum induction melting of steel. Journal of the Iron and Steel Institute. 1, 11-15.
[19] Labaj, J. (2010). Copper evaporation kinetics from liquid iron. Wydawnictwo Oldprint. (in Polish).
[20] Ozberk, E. & Guthrie, R. (1985). Evaluation of vacuum induction melting for copper refining. Transactions of the Institution of Mining and Metallurgy, Section C: Mineral Processing and Extractive Metallurgy. 94, 146-157.
[21] Ozberk, E. & Guthrie, R. (1986). A kinetic model for the vacuum refining of inductively stirred copper melts. Metallurgical Transactions B. 17, 87-103.
[22] Przyłucki, R., Golak, S., Oleksiak, B. & Blacha, L. (2012). Influence of an induction furnace's electric parameters on mass transfer velocity In the liquid phase. Metalurgija. 1, 67-70.
[23] Blacha, L., Przylucki, R., Golak, S. & Oleksiak, B. (2011). Influence of the geometry of the arrangement inductor - crucible to the velocity of the transport of mass in the liquid metallic phase mixed inductive. Archives of Civil and Mechanical Engineering. 11, 171-179. DOI: 10.1016/S1644-9665(12)60181-2.
[24] Blacha, L., Golak, S., Jakovics, S. & Tucs, A. (2014). Kinetic analysis of aluminum evaporation from Ti-6Al-7Nb. Archives of Metallurgy and Materials. 59, 275-279. DOI: 10.2478/amm-2014-0045
[25] Spitans, S., Jakovics, A., Baake, E. & Nacke, B. (2010). Numerical modelling of free surface dynamics of conductive melt in the induction crucible furnace. Magnetohydrodynamics. 46, 425-436
[26] Spitans, S., Jakovics, A., Baake, E. & Nacke, B. (2011). Numerical modelling of free surface dynamics of melt in an alternate electromagnetic field. Magnetohydrodynamics. 47, 385-397.
[27] Golak, S. & Przylucki, R. (2008). The optimization of an inductorposition for minimization of a liquid metal free surface, Przegląd Elektrotechniczny. 84, 163-164.
[28] Golak, S. & Przyłucki R. (2009). A simulation of the coupled problem of magnetohydrodynamics and a free surface for liquid metals. WIT Transactions of Engineering Science. 48, 67-76. DOI: 10.2495/MPF090061.
Go to article

Authors and Affiliations

Albert Smalcerz
ORCID: ORCID
Leszek Blacha
ORCID: ORCID
J. Łabaj
1
ORCID: ORCID

  1. Silesian University of Technology, Faculty of Materials Engineering and Metallurgy, ul. Krasińskiego 8, 40-019 Katowice, Poland
Download PDF Download RIS Download Bibtex

Abstract

This paper presents an overview of a research on six practical cases that were solved in a precise casting company where parts are cast by the mean of the low-wax casting method (investment casting) in order to decrease poor quality production. The steel cast parts production technology by the lost-wax method requires the detailed work procedures observation. On the base of statistical processing data of given types of casting products, it was possible to assess the significance of each particular checking events by using the statistical hypothesis testing. The attention was focused on wax and ceramic departments. The data in technological flow were compared before and after the implementation of the change and statistical confirmative influences were assessed. The target consisted in setting such control manners in order to get the right conditions for decreasing poor quality parts. It was evidenced that the cast part defect cause correct identification and interpretation is important.
Go to article

Bibliography

[1] Elbel, T., Havlíček, F., Jelínek, P., Levíček, P., Rous, J., Stránský, K. (1992). Defects of iron alloy castings (classification, causes and prevention). Brno: MATECS. (in Czech).
[2] Nenadál, J. (2004). Measurement in quality management systems. Praha: Management Press. (in Czech).
[3] Lakomá, R., Čamek, L. (2013). Possibilities for quality control of casting products . In 22nd International Conference on Metallurgy and Materials, Metal, 15th-17th May 2013 (p. 40). Brno, Czech Republic, TANGER s. r. o. Ostrava. ISBN 978-80-87294-39-0.
[4] Plura, J. (2001). Planning and continuous quality improvement. Praha: Computer Press. (in Czech).
[5] Čamek, L., Lichý, P., Kroupová, I., Duda, J., Beňo, J., Korbáš, M., Radkovský, F., Bliznyukov, S. (2016). Effect of cast steel production metallurgy on the emergence of casting defect. Metalurgija. 55(4), 701-704. ISSN 0543-5846.
[6] Jezierski, J., Dojka, K., Kubiak, K., et al. (2016). Experimental approach for optimization of gating system in castings. In 25th International Conference on Metallurgy and Materials, Metal 25th-27th May (pp. 104-109). Brno, Czech Republic, TANGER s. r. o. Ostrava. ISSN 0543-5846.
[7] Jaromin, M., Dojka, R., Jezierski, J., Dojka, M. (2019). Influence of Type and Shape of the Chill on Solidification Process of Steel Casting. Archives of Foundry Engineering. 19(1), 35-40. ISSN (1897-3310).
[8] Richtarech, L., Bolibruchova, D.; Bruna, M.; Caiss, J. (2015). Influence of Nickel Addition on Properties of Secondary AlSi7Mg0.3 Alloy‎. Archives of Foundry Engineering. 15(2), 95-98. ISSN (1897-3310). DOI: 10.1515/afe-2015-0046.
[9] Merta, V., Lána, I. (2020). Manufacturing of Cast-metal Sponges from Copper Alloys. Materiali in Technologije. 54(1), 117-119. DOI: 10.17222/mit.2019.159.
Go to article

Authors and Affiliations

R. Lakomá
1
L. Čamek
2
P. Lichý
2
ORCID: ORCID
I. Kroupová
1
ORCID: ORCID
F. Radkovský
1
ORCID: ORCID
T. Obzina
1

  1. VSB - Technical university of Ostrava, Czech Republic
  2. Brno University of Technology, Czech Republic
Download PDF Download RIS Download Bibtex

Abstract

Aiming at the problems of delay and couple in the sintering temperature control system of lithium batteries, a fuzzy neural network controller that can solve complex nonlinear temperature control is designed in this paper. The influence of heating voltage, air inlet speed and air inlet volume on the control of temperature of lithium battery sintering is analyzed, and a fuzzy control system by using MATLAB toolbox is established. And on this basis, a fuzzy neural network controller is designed, and then a PID control system and a fuzzy neural network control system are established through SIMULINK. The simulation shows that the response time of the fuzzy neural network control system compared with the PID control system is shortened by 24s, the system stability adjustment time is shortened by 160s, and the maximum overshoot is reduced by 6.1%. The research results show that the fuzzy neural network control system can not only realize the adjustment of lithium battery sintering temperature control faster, but also has strong adaptability, fault tolerance and anti-interference ability.
Go to article

Bibliography

[1] Li, H.S., Miao, Q. & Zhou, R.M. (2014). Research on control algorithm of ceramic kiln temperature control system. Journal of Wuhan University of Technology. 36(10), 135-139. DOI: 10.3963/j.issn.1671-4431.2014.10.024.
[2] Zhu, D.Q. & Jiang, K.R. (2009). Design and simulation of fuzzy neural network controller for drying process. Journal of System Simulation. 21(15), 4768-4771. DOI: 10.16182/j.cnki.joss.2009.15.079.
[3] Zhang, Z.M., Zhang, J.Y. & Feng, X.G. (2019). Design of hot blast stove temperature control system based on RBF neural network tuning. Journal of Hebei University of Science and Technology. 40(06), 503-511. DOI: 10.7535/hbkd.2019yx06007.
[4] Bai, G.Z. & Yu, J.H. (2016). PID parameter self-tuning based on improved fuzzy neural network. Computer Application Research. 33(11), 3358-3363+3368. DOI: 10.3969/j.issn.1001-3695.2016.11.035.
[5] Li, C.L. & Huang, C.Z. (2010). Design of temperature control system based on fuzzy neural network. Microcomputer Information. 26(07), 75-76+98. DOI: 10.3969/j.issn.2095-6835.2010.07.031.
[6] Li, G.Q., Tong, S.H. & Lu, L.X. (2013). Analysis of the temperature field in a continuous sintering furnace for solar cells. Computer Simulation. 30(01), 188-192+218. DOI: 10.3969/j.issn.1006-9348.2013.01.043.
[7] Huang, B., Xie, G.J., Liang, W.S. & Zhang, J.W. (2018). Application of heating furnace temperature control system based on hybrid fuzzy PID. Electric Drive. 48(02), 43-46. DOI: 10.19457/j.1001-2095.20180208.
[8] Zhou, G.L., Peng, Y.F. & Dong, H.S. (2007). Design of adaptive fuzzy PID controller based on T-S model. Industrial Instrumentation and Automation. 2, 22-25. DOI: CNKI: SUN: GYZD.0.2007-02-005.
[9] Tan, M., Cheng, C.H. & Lu, C. (2006). Research on the temperature control system of vacuum sintering furnace based on neural network. Measurement and Control Technology. 2, 31-32+53. DOI: 10.19708/j.ckjs.2006.02.010.
[10] Wang, J.P. & Ku, M.S. (2010). Application of FNN on atmospheric heating furnace of distillation unit. Computer Measurement and Control. 18(11), 2649-2651. DOI: 10.16526/j.cnki.11-4762/tp.2010.11.003. [11] Chen, B.F., Yin, P.L. & Ma, L. (2010). Research on temperature control system based on fuzzy neural network. Computer and Digital Engineering. 38(07), 54-57. DOI: 10.3969/j.issn.1672-9722.2010.07.016.
[12] Li, M.H. & Li, Z.Q. (2012). Research on Decoupling Control Strategy of Injection Molding Machine Barrel Temperature Based on Neural Network. Ceramics. 4, 17-19. DOI: 10.19397/j.cnki.ceramics.2012.04.004.
[13] Hu, Y.N. & Ma, W.M. (2017). Research and application of paper quantitative moisture control strategy based on FNN decoupling. China Paper. 36(07), 48-53. DOI: 10.11980/j.issn.0254-508X.2017.07.009. [14] Zhang, L., Zhang, J.C., Han, H.G. & Qiao, J.F. (2020). Process control of biochemical phosphorus removal in sewage treatment based on fuzzy neural network. CIESC Journal. 71(03). 1217-1225. DOI: 10.11949/0438-1157.20191514.
[15] Tao, X.M., Luo, L. & Liu, Z.G. (2015). Research and simulation of injection molding machine barrel temperature control algorithm based on segmented PID. Plastics. 44(03), 68-70. DOI: CNKI: SUN: SULA.0.2015-03-022.
[16] Zhou, P.Q. (2016). Research on synchronization control technology of double winches based on fuzzy neural network. Machine Design and Manufacture. 9, 64-68. DOI: 10.19356/j.cnki.1001-3997.2016.09.017.
[17] Li, J.J., Xu, Y., Zhang, G., Wei, Z.Y. & Zhang, Y.B. (2015). Irrigation controller design based on BP neural network prediction and fuzzy control. Machine Design and Research. 31(05), 150-154. DOI: 10.13952/j.cnki.jofmdr. 2015.0207.
[18] Luo, C.N., Hao, R.K. & Yang, W. (2018). Boiler temperature control simulation in industrial production process. Computer simulation. 35(09), 358-362. DOI: 10.3969/j.issn.1006-9348.2018.09.074.
[19] Zhao, J. & Xu, H. (2016). Computer simulation study on segmental control of barrel temperature of injection molding machine. Synthetic Resin and Plastics. 33(05), 61-63. DOI: 10.3969/j.issn.1002-1396.2016.05.018.
Go to article

Authors and Affiliations

Zou Chaoxin
1
Li Rong
1
Xie Zhiping
1
Su Ming
1
Zeng Jingshi
2
Ji Xu
1
Ye Xiaoli
1
Wang Ye
1

  1. Guizhou Normal University, China
  2. Guizhou Zhenhua New Material Co., Ltd., China
Download PDF Download RIS Download Bibtex

Abstract

The paper presents the results of research related to the possibility of inoculation of the AZ91 magnesium alloy casted into ceramic moulds by gadolinium. Effects of gadolinium content (0.1–0.6 wt%) on microstructure of the AZ91 alloy under as-cast state were investigated. The influence of the inoculator on the formation of the microstructure investigated by means of the thermal and derivative analysis by analysing the thermal effects arising during the alloy crystallization resulting from the phases formed. The degree of fragmentation of the microstructure of the tested alloys was assessed by means of the light microscopy studies and an image analysis with statistical analysis was performed. Conducted analyses have aimed at examining on the effect of inoculation of the gadolinium on the differences between the grain diameters and average size of each type of grain by way of measuring their perimeters of all phases, preliminary αMg and eutectics αMg+γ(Mg17Al12) in the prepared examined material.
Go to article

Bibliography

[1] Wang, Y.N. & Huang, J.C. (2007). The role of twinning and untwining in yielding behavior in hot-extruded Mg-Al-Zn. Alloy Acta Materialia. 55(3), 897-905. DOI: 10.1016/ j.actamat.2006.09.010.
[2] Yu, Zhang et. al (2017). Effects of samarium addition on as-cast microstructure, grain fragmentation and mechanical properties of Mg-6Zn-0.4Zr magnesium alloy. Journal of Rare Earths. 167(1), 31-33. DOI: 10.1016/S1002-0721(17)60939-6.
[3] Cao, F.Y, Song, G.L. & Atrens, A. (2016). Corrosion and passivation of magnesium alloys. Corrosion Science, 111(10), 835-845. DOI: 10.1016/j.corsci.2016.05.041.
[4] Mao, X., Yi, Y., Huang, S. & He, H. (2019). Bulging limit of AZ31B magnesium alloy tubes in hydroforming with internal and external pressure. The International Journal of Advanced Manufacturing Technology. 101, 2509-2517. DOI: https://doi.org/10.1007/s00170-018-3076-5.
[5] Władysiak, R. & Kozuń, A. (2015). Structure of AlSi20 alloy in heat treated die casting. Archives of Foundry Engineering.15(1), 113-118. DOI: 10.1515/afe-2015-0021.
[6] Rapiejko, C., Pisarek, B. & Pacyniak, T. (2017). Effect of intensive cooling of alloy AZ91 with a chromium addition on the microstructure and mechanical properties of the casting. Archives of Metallurgy and Materials. 62(4), 2199-2204. DOI: 10.1515/amm-2017-0324.
[7] Zhao, H.L., Guan, S.K. & Zheng, F.Y. (2007). Effects of Sr and B addition on microstructure and mechanical properties of AZ91 magnesium alloy. Journal of Materials Research. 22, 2423-2428. DOI: 10.1557/jmr.2007.0331.
[8] Bonnah, R.C., Fu, Y. & Hao, H. (2019). Microstructure and mechanical properties ofAZ91 magnesium alloy with minor additions of Sm, Si and Ca elements. China Foundry. 16(5), 319-325. DOI: 10.1007/s41230-019-9067-9.
[9] Jafari, H. & Amiryavari, P. (2016). The effects of zirconium and beryllium on microstructure evolution, mechanical properties and corrosion behaviour of as-cast AZ63 alloy. Materials Science & Engineering A. 654, 161-168 DOI: 10.1016/j.msea.2015.12.034.
[10] Boby, A., Ravikumar, K.K., Pillai, U.T.S. & Pai, B.C. (2013). Effect of antimony and yttrium addition on the high temperature properties of AZ91 magnesium alloy. Procedia Engineering 55. 355(5), 98-102. DOI: 10.1016/j.proeng. 2013.03.226.
[11] Huang, W., Yang, X., Mukai, T. & Sakai, T. (2019). Effect of yttrium addition on the hot deformation behaviors and microstructure development of magnesium alloy. Journal of Alloys and Compounds. 786, 118-125. DOI: 10.1016/ j.jallcom.2019.01.269.
[12] Pourbahari, B., Mirzadeh, H., Emamy, M. & Roumina, R. (2018). Enhanced ductility of afine-grained Mg-Gd-Al-Zn magnesium alloy by hot extrusion. Advanced Engineering Materials. 20, 1701171. DOI: 10.1002/adem.201701171.
[13] Tardif, S., Tremblay, R. & Dubé, D. (2010). Influence of cerium on the microstructure and mechanical properties of ZA104 and ZA104 + 0.3Ca magnesium alloys. Material Science and Engineering A. 527, 7519-7529. DOI: 10.1016/j.msea.2010.08.082.
[14] Wang, X.J. et al. (2018). What is going on in magnesium alloys? Journal of Materials Science & Technology. 34(2), 245-247. DOI: 10.1016/j.jmst.2017.07.019.
[15] Nan, J. et. al (2016) Effect of neodymium, gadolinium addition on microstructure and mechanical properties of AZ80 magnesium alloy. Journal of Rare Earths. 34(6), 632-637. DOI: 10.1016/S1002-0721(16)60072-8.
[16] Miao, Y., Yaohui, L., Jiaan, L. & Yulai, S. (2014). Corrosion and mechanical properties of AM50 magnesium alloy after being modified by 1 wt.% rare earth element gadolinium. Journal of Rare Earth. 723, 558-563. DOI: 10.1016/S1002-0721(14)60108-3.
[17] Mingbo, Y., Caiyuan, Q., Fusheng, P. & Tao, Z. (2011). Comparison of effects of cerium, yttrium and gadolinium additions on as-cast microstructure and mechanical properties of Mg-3Sn-1Mn magnesium alloy. Journal of Rare Earths. 29(6), 550-557. DOI: 10.1016/S1002-0721(10)60496-6.
[18] Sumida, M., Jung, S. & Okane, T. (2009). Microstructure, solute partitioning and material properties of gadolinium-doped magnesium alloy AZ91D. Journal of Alloys and Compounds. 475. 903-910. DOI: 10.1016/j.jallcom. 2008.08.067/
[19] Pietrowski, S. & Rapiejko, C. (2011). Temperature and microstructure characteristics of silumin casting AlSi9 made with investment casting method. Archives of Foundry Engineering. 11(3), 177-186.
[20] PN-EN 1753:2001. Magnesium and magnesium alloys. Magnesium alloy ingots and castings.
[21] Rapiejko, C., Pisarek, B, Czekaj, E. & Pacyniak, T. (2014). Analysis of AM60 and AZ91 Alloy Crystallisation in ceramic moulds by thermal derivative analisys (TDA). Archive of Metallurgy and Materials. 59(4) DOI: 10.2478/amm-2014-0246.
Go to article

Authors and Affiliations

C. Rapiejko
1
ORCID: ORCID
D. Mikusek
1
P. Just
1
T. Pacyniak
1
ORCID: ORCID

  1. Lodz University of Technology, Department of Materials Engineering and Production Systems, ul. Stefanowskiego 1, 90-924 Łódź, Poland
Download PDF Download RIS Download Bibtex

Abstract

Chromium low alloyed steel substrate was subjected to aluminizing by hot dipping in pure aluminium and Al-Si eutectic alloy at 750°C and 650°C respectively, for dipping time up to 45 minutes. The coated samples were subjected for investigation using an optical microscope, scanning electron microscopy (SEM), Energy-dispersive X-ray analyzer (EDX) and X-ray diffraction (XRD) technique. Cyclic thermal oxidation test was carried out at 500°C for 72 hours to study the oxidation behaviour of hot-dipped aluminized steel. Electrochemical corrosion behavior was conducted in 3wt. %NaCl aqueous solution at room temperature. The cyclic thermal oxidation resistance was highly improved for both coating systems because of the formation of a thin protective oxide film in the outermost coating layer. The gain in weight was decreased by 24 times. The corrosion rate was decreased from 0.11 mmpy for uncoated specimen to be 2.9 x10-3 mmpy for Aluminum coated steel and 5.7x 10-3 mmpy for Al-Si eutectic coated specimens. The presence of silicon in hot dipping molten bath inhabit the growth of coating intermetallic layers, decrease the total coating thickness and change the interface boundaries from tongue like shape to be more regular with flatter interface. Two distinct coating layers were observed after hot dipping aluminizing in Al bath, while three distinct layers were observed after hot dipping in Al-Si molten bath.
Go to article

Bibliography

[1] Kuruveri, U.B., Huilgol, P., Joseph, J. (2013). Aluminising of mild steel plates. ISRN Metallurgy. 1-6.
[2] Isiko, M.B. (2012). A luminizing of plain carbon steel: Effect of temperature on coating and alloy phase morphology at constant holding time. Norway. Institute for material technology. 1-2.
[3] Davis, J.R. (1990). Surface engineering. vol. 5 of ASM Metals Handbook. Ohio, USA Materials Park.
[4] Ahmad, Z. (2006). Principles of corrosion engineering and corrosion control. London: UK. Elsevier. 17.
[5] Burakowski T., Weirzchok, T. (2000). S urface engineering of Metals- Principles, Equipments, Technologies. CRC Press, London, UK.
[6] Pattankude1, B.G., Balwan,. A.R. (2019). A review on coating process. International Research Journal of Engineering and Technology (IRJET). 06(3), 7980.
[7] Huilgol, P., Bhat, S. & Bhat, K.U. (2013). Hot-dip aluminizing of low carbon steel using Al- 7Si-2Cu alloy baths. Journal of Coatings. 2013, 1-6.
[8] Lin, M.-B. Wang, C.-J. & Volinsky, A.A. (2011). Isothermal and thermal cycling oxidation of hot- dip aluminide coating on flake/spheroidal graphite cast iron. Surface and Coatings Technology. 206, 1595-1599.
[9] Dngik Shin, Jeong-Yong Lee, Hoejun Heo, & Chung-Yun Kang. (2018). Formation procedure of reaction phases in Al hot dipping process of steel. Metals journal. 1.
[10] Yu Zhang, Yongzhe Fan, Xue Zhao, An DU, Ruina Ma, & Xiaoming Cao. (2019). Influence of graphite morphology on phase, microstructure and properities of hot dipping and diffusion aluminizing coating on flake/spheroidal graphite cast iron. Metals journal. 1.
[11] Voudouris, N. & Angelopoulos, G. (1997). Formation of aluminide coatings on nickel by a fluidized bed CVD process. Surface Modification Technologies XI. 558-567.
[12] Wang, D. & Shi, Z. (2004). Aluminizing and oxidation treatment of 1Cr18Ni9 stainless steel. Applied surface science. Volume (227). 255-260.
[13] Murakami, K., Nishida, N., Osamura, K. & Tomota, Y. (2004). Aluminization of high purity iron by powder liquid coating. Acta Materialia. 52(5), 1271-1281.
[14] Cheng, W.-J. & Wang, C.-J. (2013). High-temperature oxidation behavior of hot-dipped aluminide mild steel with various silicon contents. Applied surface science. 274. 258-265.
[15] Mishra, B., Ionescu, M. & Chandra, T. (2013). The effect of Si on the intermetallic formation during hot dip aluminizing. Advanced Materials Research. Volume 922, 429-434.
[16] Kee-Hyun, et. Al. (2006). Observations of intermetallic compound formation of hot dip aluminized steel. Materials Science Forum. 519-521, 1871-1875.
[17] Fry, A., Osgerby, S., Wright, M. (2002). Oxidation of alloys in steam environments. United Kingdom: NPL Materials Centre. 6.
[18] Scott, D.A. (1992). Metallography and microstructure in ancient and historic metals. London. Getty publications. 57-63.
[19] Lawrence J. Korb, Rockwell, David L. Olson. (1992). ASM Handbook Vol 13: Corrosion: Fundametals, Testing and Protection. Florida, USA: ASM International Handbook Committee.
[20] Nicholls, J. E. (1964). Corr. Technol. 11.16.
[21] Azimaee, H. et. al. (2019). Effect of silicon and manganese on the kinetics and morphology of the intermetallic layer growth during hot-dip aluminizing. Surface and Coatings Technology. 357. 483-496.
[22] Sun Kyu Kim, (2013). Hot-dip aluminizing with silicon and magnesium addition I. Effect on intermertallic layer thickness. Journal of the Korean Institute of Metals and Materials. 51(11), 795-799.
[23] Springer, H., Kostka, A., Payton, Raabe, D., Kaysser, A. & Eggeler, G. (2011). On the formation and growth of intermetallic phases during interdiffusion growth between low-carbon steel and aluminum alloys. Acta Materialia. 59, 1586-1600.
[24] Kab, M., Mendil, S. & Taibi, K. (2020). Evolution of the microstructure of intermetallic compounds formed on mild steel during hot dipping in molten Al alloy bath. M etallography, Microstructure and Analysis. Journal 4.
[25] Bahadur A. & Mohanty, O.N. (1991). Materials Transaction. JIM. 32(11), 1053-1061.
[26] Bouche, K., Barbier, F. & Coulet, A. (1998). Intermetallic compound layer growth between solid iron and molten aluminium. Materials Science and Engineering A. 249(1-2), 167-175.
[27] Maitra, T. & Gupta, S.P. (2002). Intermetallic compound formation in Fe–Al–Si ternary system: Part II. Materials Characterization. 49(4), 293-311.
[28] Nychka, J.A. & Clarke, D.R. (2005). Quantification of aluminum outward diffusion during oxidation of FeCrAl alloys. Oxidation of Metals. 63 (Nos.5/6), 325-351.
[29] Lars, P.H. et. All. (2002). Growth kinetics and mechanisms of aluminum-oxide films formed by thermal oxidation of aluminum. Journal of Applied Physics. 92(3), 1649-1656.
[30] Murray, J.L. (1992). Fe–Al binary phase diagram, in: H. Baker (Ed.), Alloy Phase Diagrams. ASM International. OH- USA. Materials Park. 54.

Go to article

Authors and Affiliations

G.M. Attia
1
W.M.A. Afify
1
M.I. Ammar
1

  1. Metallurgical and Materials Engineering Department, Faculty of Petroleum and Mining Engineering Suez University, Egypt
Download PDF Download RIS Download Bibtex

Abstract

The present paper is concerned with the practical interconnection between virtual engineering tools and additive model manufacturing technologies and the subsequent production of a ceramic shell by rapid prototyping with the use of Cyclone technology to produce the aluminium casting prototype. Prototypes were developed as part of the student formula project, where several parts originally produced by machining were replaced by castings. The techniques of topological optimization and the combination with the tools of the numerical simulation were used to optimise the virtual prototype before a real production of the first prototype. 3D printing of wax pattern ensured direct and fast assembly of the cluster without any additional operations and troubles during dewaxing. The shell was manufactured in 6 hours thanks to a system of quick-drying of individual layers of ceramic shell. It has been verified that the right combination of individual virtual tools with the rapid prototyping can shorten the development time and delivery of the first prototypes from a few months to a few weeks.
Go to article

Bibliography

[1] Xiao, A., Bryden, K.M. (2004). Virtual engineering: A vision of the next-generation product realization using virtual reality technologies. Proceedings of the ASME 2004 Design Engineering Technical Conferences – DETC’04, 28 September – 2 October, pp 1-9.Salt Lake City, Utah, #57698.
[2] Pekkola, S. & Jäkälä, M. (2007) From technology engineering to social engineering: 15 years of research on virtual worlds. The DATA BASE for Advances in Information Systems. 38(4), 11-16.
[3] Bao, Jin, J.S., Gu, Y., Yan, M.Q. & Ma, J.Q. (2002). Immersive virtual product development. Journal of Materials Processing Technology. 129(1-3), 592-596. DOI: 10.1016/S0924-0136(02)00655-6.
[4] Van der Auweraer, H. (2010). Virtual engineering at work: The challenges for designing intelligent products. In: Proceedings of the TMCE 2010 Symposium, April 12-16, (pp. 3-18), Ancona, Italy.
[5] Stawowy, A., Wrona, R., Brzeziński, M. & Ziółkowski, E. (2013). Virtual factory as a method of foundry design and production management. Archives of Foundry Engineering. 13(1), 113-118. DOI: 10.2478/afe-2013-0022
[6] Dépincé, P., Chablat, D., Woelk, P.O. (2004) Virtual manufacturing: tools for improving design and production, Dans International Design Seminar - CIRP International Design Seminar, Egypt.
[7] Kumar, P., Ahuja, I.P.S. & Singh, R. (2013). Framework for developing a hybrid investment casting process. Asian Review of Mechanical Engineering, 2(2), 49-55.
[8] Kügelgen, M. (2008). From 7 days to 7 hours – Investment casting parts within the shortest time, 68th WFC - World Foundry Congress, 7th - 10th February, 2008, (pp. 147-151).

Go to article

Authors and Affiliations

V. Krutiš
1
ORCID: ORCID
P. Šprta
1
V. Kaňa
1
ORCID: ORCID
A. Zadera
1
J. Cileček
2

  1. Brno University of Technology, Czech Republic
  2. Alucast s.r.o., Czech Republic
Download PDF Download RIS Download Bibtex

Abstract

For research purposes and to demonstrate the differences between materials obtained from the carbonaceous additives to classic green moulding sands, five lustrous carbon carriers available on the market were selected. The following carbonaceous additives were tested: two coal dusts (CD1 and CD2), two hydrocarbon resins (HR1 and HR2) and amorphous graphite (AG1). The studies of products and material effects resulting from the high-temperature pyrolysis of lustrous carbon carriers were focused on determining the tendency to gas evolution, including harmful compounds from the BTEX group (benzene, toluene, ethylbenzene and xylene). Moreover, the content of lustrous carbon (LC), the content of volatile matter and loss on ignition (LOI) of the carbonaceous additives were tested. The solid products formed during high-temperature pyrolysis were used for the quantitative and qualitative evaluation of elemental composition after the exposure to temperatures of 875oC in a protective atmosphere and 950oC in an oxidizing atmosphere. The conducted studies have indicated the necessity to examine the additives to classic green moulding sands, which is of particular importance for the processing, rebonding and storage of waste sand. The studies have also revealed some differences in the quantitative and qualitative composition of elements introduced to classic moulding sands together with the carbonaceous additives that are lustrous carbon carriers. It was also considered necessary to conduct a research on lustrous carbon carriers for their proper and environmentally friendly use in the widely propagated technology of classic green sand system.
Go to article

Bibliography

[1] Said, R.M., Kamal, M.R.M., Miswan, N.H. & Ng, S.J. (2018). Optimization of Moulding Composition for Quality Improvement of Sand Casting. Journal of Advanced Manufacturing Technology (JAMT). 12(1), 301-310.
[2] Saikaew, C. & Wiengwiset, S. (2012). Optimization of molding sand composition for quality improvement of iron castings. Applied Clay Science. 67, 26-31. DOI: 10.1016/j.clay.2012.07.005.
[3] Kwaśniewska-Królikowska, D. & Holtzer, M. (2013). Selection criteria of lustrous carbon carriers in the aspect of properties of greensand system. Metalurgija. 52(1), 62-64.
[4] LaFay, V. & Crandell, G. (2009). Three Methods of Reducing Seacoal by Adding Graphite into Greensand Molds. Transactions of the American Foundrymen's Society. 117, 789.
[5] Lewandowski J.L. (2000). Lustrous carbon carrier, Przegląd Odlewnictwa, 10, 384-386. (in Polish)
[6] Lewandowski, J.L. (1998). The effect of coal dust on the toxicity of classic moulding sand. Przegląd Odlewnictwa, 10 322-325. (in Polish)
[7] Jelínek, P. & Beňo, J. (2008). Morphological forms of carbon and their utilizations at formation of iron casting surfaces. Archives of Foundry Engineering. 8(2008), 67-70.
[8] Major-Gabryś, K. (2019). Environmentally Friendly Foundry Molding and Core Sands. Journal of Materials Engineering and Performance. 28(7), 3905-3911. DOI: 10.1007/s11665-019-03947-x.
[9] Holtzer, M. (2012). Technologies of moulding and core sands in the aspect of environmental protection. 3rd Conference Hüttenes-Albertus Poland. 19-40. (in Polish)
[10] Holtzer, M., Bobrowski, A., Grabowska, B., Eichholzb, S., & Hodorc, K. (2010). Investigation of carriers of lustrous carbon at high temperatures by infrared spectroscopy (FTIR). Archives of Foundry Engineering. 10(4), 61-68.
[11] Lewandowski, J.L. (1997). Materials for Foundry Moulds. Kraków: WN Akapit. ISBN: 83-7108-21-2. (in Polish)
[12] Holtzer, M. (2005). Can we eliminate coal dust from classic moulding sands? Przegląd Odlewnictwa. 12, 794-798. (in Polish).
[13] Naro, R.L. (2002). Formation and control of lustrous carbon surface defects in iron and steel castings. Transactions-American Foundrymens Society. 1, 815-834.
[14] Naro, R.L. (2002). An Update on the Formation and Control of Lustrous Carbon Surface Defects in Iron Castings. Ductile Iron News. 3.
[15] Campbell, J., & Naro, R.L. (2010). Lustrous Carbon on Gray Iron (10-136). Transactions of the American Foundrymen's Society, 118, 277.
[16] Jelinek, P., Buchtele, J., Fiala, J. (2004). Lustrous carbon and pyrolysis of carbonaceous additives to bentonite sands, Casting Technology, 66 World Foundry Congress, 455-467.
[17] Engelhardt, T. (2016). Low-emission additives to bentonite-bonded moulding sands. Przegląd Odlewnictwa. 66, 220-223. (in Polish)
[18] Holtzer, M., Żymankowska-Kumon, S., Kubecki, M., & Kwaśniewska-Królikowska, D. (2013). Harmfulness assessment of resins used as lustrous carbon carriers in bentonite moulding sands. Archives of Metallurgy and Materials. 58(3), 817-822. DOI: 10.2478/amm-2013-0078M.
[19] Stefański, Z. (2008). New coal dust substitutes for bentonite moulding sands used in manufacture of castings from malleable iron and aluminium alloys. Transactions of the Foundry Research Institute. 4, 5-18.
[20] Wang, Y., Huang, H., Cannon, F.S., Voigt, R.C., Komarneni, S. & Furness, J.C. (2007). Evaluation of volatile hydrocarbon emission characteristics of carbonaceous additives in green sand foundries. Environmental Science & Technology. 41(8), 2957-2963.
[21] Wang, Y., Cannon, F.S. & Li, X. (2011). Comparative analysis of hazardous air pollutant emissions of casting materials measured in analytical pyrolysis and conventional metal pouring emission tests. Environmental Science & Technology. 45(19), 8529-8535. DOI: 10.1021/es2023048.
[22] Jelinek, P., Buchtele, J., Kriz, V., Nemecek, S., Kriz, A., & Fiala, J. (2002). Morphology and Formation of Pyrolytic Carbon in Moulding Mixtures. Acta Metallurgica Slovaca. 8(4), 415-422.
[23] Michta-Stawiarska, T. (1998). Difficulties in stabilizing the properties of classic molding sands. Krzepnięcie Metali i Stopów. 35, PAN - Oddział Katowice PL. ISSN 0208-9386 (in Polish)
[24] Ji, S., Wan, L., & Fan, Z. (2001). The toxic compounds and leaching characteristics of spent foundry sands. Water, Air, and Soil Pollution. 132(3-4), 347-364, DOI: 10.1023/A:1013207000046.
[25] Orlenius, J. (2008). Factors Related to the Formation of Gas Porosity in Grey Cast Iron: Investigation of Core Gas Evolution and Gas Concentrations in Molten Iron. Research Series from Chalmers University of Technology, ISSN 1653-8891, Licentiate Theses.
[26] Bobrowski, A. & Grabowska, B. (2012). The impact of temperature on furan resin and binders structure. Metallurgy and Foundry Engineering. 38, 73-80.
[27] Poljanšek, I. & Krajnc, M. (2005). Characterization of phenol-formaldehyde prepolymer resins by in line FT-IR spectroscopy. Acta Chimica Slovenica. 52, 238-244.
[28] Bobrowski, A., Drożyński, D., Grabowska, B., Kaczmarska, K., Kurleto-Kozioł, Ż., & Brzeziński, M. (2018). Studies on thermal decomposition of phenol binder using TG/DTG/DTA and FTIR-DRIFTS techniques in temperature range 20–500° C. China Foundry. 15(2), 145-151.
[29] Liu, L., Cao, Y. & Liu, Q. (2015). Kinetics studies and structure characteristics of coal char under pressurized CO2 gasification conditions. Fuel. 146, 103-110.
[30] Sonibare, O.O., Haeger, T., & Foley, S.F. (2010). Structural characterization of Nigerian coals by X-ray diffraction, Raman and FTIR spectroscopy. Energy. 35(12), 5347-5353.
[31] Schwan, J., Ulrich, S., Batori, V., Ehrhardt, H. & Silva, S.R.P. (1996). Raman spectroscopy on amorphous carbon films. Journal of Applied Physics. 80(1), 440-447.
Go to article

Authors and Affiliations

J. Kamińska
1
ORCID: ORCID
M. Stachowicz
2
ORCID: ORCID
M. Kubecki
3

  1. Łukasiewicz Research Network – Krakow Institute of Technology, Poland
  2. Wroclaw University of Technology, Faculty of Mechanical Engineering, Poland
  3. Łukasiewicz Research Network – Institute for Ferrous Metallurgy, Gliwice, Poland
Download PDF Download RIS Download Bibtex

Abstract

The paper presents results of research on steel castings GX120Mn13 (L120G13 by PN-89/H-83160), zone-reinforced by elektrocorundum particles (Al2O3), with a grain size from 2 to 3.5 mm. Studies revealed continuity at interface between composite components and formation of a diffusion zone in the surface layer of electrocorundum grains. In the area of this zone, simple manganese segregation and reverse iron and chromium segregation were found. The transfer of these elements from cast steel to electrocorundum grains resulted superficial depletion in aluminum and oxygen in this area. No porosity was observed at the interface between two components of the composite. We found it very beneficial from an exploitation point of view, as confirmed by the study of resistance to abrasive wear.
Go to article

Bibliography

[1] Matthews, F.L., Rawlings, R.D. (1999). Composite Materials. Engineering and Science. CRC Press: Boca Raton, FL, USA.
[2] Kocich, R., Kunčická, L., Král, P. & Strunz, P. (2018). Characterization of innovative rotary swaged Cu-Al clad composite wire conductors. Materials Design. 160, 828-835. Materials 2020. 13, 4161, p. 13 of 15.
[3] Kunčická, L., Kocich, R., Dvořák, K. & Macháčková, A. (2019). Rotary swaged laminated Cu-Al composites. Effect of structure on residual stress and mechanical and electric properties. Materials Science Engineering A. 742, 743-750.
[4] Kunčická, L., Kocich, R. (2018) Deformation behaviour of Cu-Al clad composites produced by rotary swaging. IOP Conf. Ser. Mater. Sci. Eng. 369, Kitakyushu City, Japan.
[5] Clyne, T.W., Withers, P.J. (1993) An Introduction to Metal Matrix Composites. Cambridge University Press: New York, NY, USA.
[6] Tjong, S. & Ma, Z. (2000). Microstructural and mechanical characteristics of in situ metal matrix composites. Materials Science Engineering R: Reports 29, 49-113.
[7] Górny, Z., Sobczak, J. (2005). Modern casting materials based on non-ferrous metals. Krakow. Ed. ZA-PIS.
[8] Sobczak, J. & Sobczak, N. (2001). Pressure infiltration of porous fibrous structures with aluminum and magnesium alloys. Composites. 1(2), 155-158.
[9] Klomp, J. (1987). Fundamentals of diffusion bonding. Amsterdam Ed. Ishida, Elsevier Science Publishers, 3-24.
[10] Kaczmar, J., Janus, A., Samsonowicz, Z. (1997). Influence of technological parameters on production of selected machine parts reinforced with ceramic fibers. Reports of Institute of Machine Technology and Automation of Wrocław University of Science and Technology. SPR No 5.
[11] Kaczmar, J., Janus, A., Kurzawa, A. (2002). Development of basics technology of manufacturing machine and device parts from aluminum composites reinforced with zones of ceramic particles. Reports of Institute of Machine Technology and Automation of Wrocław University of Science and Technology. SPR No 11.
[12] Dmitruk, A.G., Naplocha, K., Żak, A. M., Strojny-Nędza, A., Dieringa, H. & Kainer, K. (2019). Development of pore-free Ti-Si-C MAX/Al-Si composite materials manufactured by squeeze casting infiltration. Journal of Materials Engineering and Performance. 28(10), 6248-6257.
[13] Maj, J., Basista, M., Węglewski, W., Bochenek, K., Strojny-Nędza, A., Naplocha, K., Panzner, T., Tatarková, M., Fiori, F. (2018). Effect of microstructure on mechanical properties and residual stresses in interpenetrating aluminum-alumina composites fabricated by squeeze casting. Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing. 715,154-162.
[14] Szajnar, J., Wróbel, P., Wróbel, T. (2008). Model castings with composite surface layer - application. Archive of Foudry Enginnering. 8(3), 105-110.
[15] Gawroński, J., Szajnar, J., Wróbel, P. (2005). Surface composite layers of cast iron - ceramic particles. Archive of Foundry. 5(17), 107-114.
[16] Marcinkowska, J. (1986). Wear-resistant casting coatings on cast steel. Solidification of Metals and Alloys. 6, 37-42.
[17] Baron, Cz., Gawroński, J. (2006). Abrasive wear resistance of sandwich composites based on iron alloys. Composites. 6(3), 45-49.
[18] Operation and maintenance documentation of test stand T-07.
Go to article

Authors and Affiliations

Daniel Medyński
ORCID: ORCID
A.J. Janus
1

  1. Witelon State University of Applied Science in Legnica ul. Sejmowa 5A, 59 – 220 Legnica, Poland
Download PDF Download RIS Download Bibtex

Abstract

Finite Element Method FEM via commercially available software has been used for numerical simulation of the compaction process of bentonite-bonded sand mould. The mathematical model of soil plasticity which involved Drucker-Prager model match with Mohr-Coulomb model was selected. The individual parameters which required for the simulation process were determined through direct shear test based on the variation of sand compactability. The novelty of this research work is that the individual micro-mechanical parameters were adopted depend on its directly proportional to the change of sand density during the compaction process. Boundary conditions of the applied load, roller and fixed constraint were specified. An extremely coarse mesh was used and the solution by time-dependent study was done for investigation of material-dependent behaviour of green sand during the compaction process. The research implemented also simulation of the desired points in sand mould to predict behaviour of moulding process, and prevent failure of the sand mould. Distance-dependent displacement and distance-dependent pressure have been determined to investigate the effective moulding parameters without spent further energy and cost for obtaining green sand mould. The obtained numerical results of the sand displacement show good agreement with the practical results.
Go to article

Bibliography

[1] Naeimi, K., Baradaran, H., Ahmadi, R. & Shekari, M. (2015). Study and simulation of the effective factors on soil compaction by tractors wheels using the finite element method. Journal of Computational Applied Mechanics. 46(2), 107-115. DOI: 10.22059/jcamech.2015.55093.
[2] Soane, B. (1990). The role of organic matter in soil compatibility: A review of some practical aspects. Soil & Tillage Research. 16(1-2), 179-201. DOI: https://doi.org/ 10.1016/0167-1987(90)90029-D.
[3] Minaei, S. (1984). Multi pass effects of wheel and track- type vehicles on soil compaction. MS Thesis, Virginia Polytechnic Institute and State University.
[4] Chen, Y. Tessier, Y. & Rauffignat, S. (1998). Soil bulk density estimation for tillage systems and soil texture. Transactions of the American Society of Agricultural and Biological Engineers. 41(4), 1601-1610.
[5] Wenzhen, L. & Junjiao, W. (2007). Numerical Simulation of Compacting Process of Green Sand Molding Based on Sand Filling. Materials Science Forum. 561-565, 879-1882. DOI: https://doi.org/10.4028/www.scientific.net/MSF.561-565.1879.
[6] Hovad, E., Larsen, P., Walther, J., Thorborg, J. & Hattel,. J.H. (2015). Flow Dynamics of green sand in the DISAMATIC moulding process using Discrete element method (DEM). IOP Conference Series Materials Science and Engineering. 84(1) 1-8. DOI: 10.1088/1757-899X/84/1/012023.
[7] Hua, L., Junjiao, W., Tianyou, H. & Hiroyasu, M. (2011). A new numerical simulation model for high pressure squeezing moulding. China foundry. 8(1) 25-29. ID: 1672-6421(2011)01-025-05.
[8] Schijndel, van, A.W.M.(2007). Integrated heat air and moisture modeling and simulation. Doctoral dissertation, Eindhoven University of Technology. https://doi.org/ 10.6100/IR622370.
[9] Terzaghi, K. (1976). Earthwork mechanics based on soil physics (in German). G. Gistel & Cie. GmbH, Wien.
[10] Tomas, J. (1991). Modeling of the flow behavior of bulk solids on the basis of the interaction forces between the particles and applications in the design of bunkers (in German). Habilitation thesis, TU Bergakademie Freiberg.
[11] Inoue, Y., Motoyama, Y., Takahashi, H., Shinji, K. & Yoshida, M. (2013). Effect of sand mold models on the simulated mold restraint force and the contraction of the casting during cooling in green sand molds. Journal of Materials Processing Technology. 213(7), 1157-1165. https://doi.org/10.1016/j.jmatprotec.2013.01.011.
[12] Kadauw, A. (2006). Mathematical modeling of the moulding material processes (in German). Doctoral dissertation, TU- Bergakademie Freiberg.
[13] Lang, H.-J., Huder, J., Amann, P., Puzrin, A.M. (1996). Soil mechanics and foundation (in German). Springer, Berlin Heidelberg.
[14] Suroso, P., Samang, L., Tjaronge, W. & Muhammad Ramli. (2016). Estimates of Elasticity and Compressive Strenght in Soil Cement Mixed With Ijuk-Aren, International Journal of Innovative Research in Advanced Engineering (IJIRAE), 3(4), 21-26.
[15] Nujid, M.M. & Taha, M.R. (2016). Soil Plasticity Model for Analysis of Collapse Load on Layers Soil. EDP Sciences, MATEC Web of Conferences. 47(03020) 1-6. DOI: 10.1051/matecconf/ 20164703020.
[16] Chen, W.F. Mizuno, E. (1990). Nonlinear Analysis in Soil Mechanics: Theory and Implementation, Elsevier Science Publishers B. V., ISBN 978-0444430434, 5-36.
[17] Bast, J., Kadauw, A. (2004). 3D-Numerical Simulation of Squeeze Moulding with the Finite element Method. Proceeding of 66th World Foundry Congress Istanbul, 247 - 258.
Go to article

Authors and Affiliations

Dheya Abdulamer
ORCID: ORCID
A. Kadauw
1 2

  1. IMKF. TU - Bergakademie Freiberg, Germany
  2. Salahddin University-Erbil, Iraq
Download PDF Download RIS Download Bibtex

Abstract

The foundry industry is looking for solutions that improve the quality of the finished product and solutions that reduce the negative impact of the industry on the natural environment [26]. This process leads to work on the use of new or previously unused materials for binders. Organic and inorganic foundry binders are replaced by renewable materials of plant origin to meet the requirements of both the foundry customers and the environmental and health and safety regulations. The aim of this work was to identify the applicability of renewable and organic malted barley binder in moulding sand technology. The influence of the malt binder content on dry tensile strength, dry bending strength, dry permeability, dry wear resistance and flowability were evaluated. The results show that the malted barley binder can be self-contained material binding the high-silica sand grains. Selected mechanical properties of moulding sands were found to increase with an increase in binder content. It was observed that malted barley binder creates smooth bonding bridges between high-silica sand grains.
Go to article

Bibliography

[1] Lewandowski, J.L., (1997). Moulding materials. Kraków: Akapit Publisher. (in Polish).
[2] Czerwinski, F., Mir, M. & Kasprzak, W. (2015). Application of cores and binders in metalcasting. International Journal of Cast Metals Research. 28(3), 129-139. DOI: 10.1179/1743133614Y.0000000140.
[3] Ferreira, S. H. G. da, J. C. E., Kumar, V. & Garza-Reyes, J. A. (2020). Benchmarking of cleaner production in sand mould casting companies. Management of Environmental Quality: An International Journal. 31(5), 1407-1435. DOI: 10.1108/MEQ-12-2019-0272.
[4] Fayomi, O.S.I. (2016). Hybrid effect of selected local binders on the moulding properties of river niger silica sand for industrial application. Journal of Nanoscience with Advanced Technology. 1(4), 19-23. DOI: 10.24218/jnat.2016.19.
[5] Yaro, S.A. & Suleiman, M.U. (2006), Cassava/guinea corn starches and soybean oil as core binders in sand casting of aluminium silicon (Al-Si)lloy. Journal of Engineering and Technology. 1(1), 47-55.
[6] Grabowska, B. & others. (2018). Influence of carbon fibers addition on selected properties of microwave-cured moulding sand bonded with BioCo2 binder. Archives of Foundry Engineering. 18(3), 152-160. DOI: 10.24425/123618.
[7] Chowdhury, S.I. Rashid, H. & Mumtaz, G.R. (2016) Comparison and CFD verification of binder effects in sand mould casting of aluminum alloy. ANNALS of Faculty Engineering Hunedoara - International Journal of Engineering. 14(1), 143-146.
[8] Manley, D. (2000). 9 - Meals, grits, flours and starches (other than wheat). Technology of Biscuits, Crackers and Cookies (Third Edition). (104–111). Red. Woodhead Publishing.
[9] Yu, W., Quek, W., Li, C., Gilbert, R. & Fox, G. (2018) Effects of the starch molecular structures in barley malts and rice adjuncts on brewing performance. Fermentation. 4(4), 103-124. DOI: 10.3390/fermentation4040103.
[10] Fox, G.P. (2009). Chemical composition in barley grains and malt quality. Genetics and Improvement of Barley Malt Quality. (63-98). Zhang G. & C. Li, Red. Berlin, Heidelberg: Springer Berlin Heidelberg. [11] Pezarski, F., Izdebska-Szanda I., Smoluchowska, E., Świder, R. & Pysz, A. (2011). Application of moulding sands with geopolymer binder in the manufacture of castings from aluminium alloys. Prace Instytutu Odlewnictwa. 51(2), 23-34. (in Polish).
[12] Stachowicz, M. Granat, K. & Nowak, D. (2012). Bending strength measurement as a method of binder quality assessment on the example of water-glass containing moulding sands. Archives of Foundry Engineering. 12(1), 175-178. (in Polish).
[13] Stachowicz, M., Granat, K. & Nowak, D. (2010). Studies on the possibility of more effective use of water glass thanks to application of selected methods of hardening. Archives of Foundry Engineering. 10 (spec.2), 135-140.
[14] Szymański, A., (2007). Soil mechanics. Warszawa: Wydawnictwo SGGW. (in Polish).
[15] Ochulorl, E.F., Ugboaja, J.O. & Olowomeye, O.A. (2019). Performance of kaolin and cassava starch as replacements for bentonite in moulding sand used in thin wall ductile iron castings. Nigerian Journal of Technology. 38(4), 947-956. DOI: 10.4314/njt.v38i4.18.
[16] Popoola, A.P.I., Abdulwahab, M. & Fayomi, O.S.I. (2012). Synergetic performance of palm oil (Elaeis guineensis) and pine oil (Pinus sylvestris) as binders on foundry core strength. International Journal of the Physical Sciences. 7(24), 3062-3066. DOI: 10.5897/IJPS12.347.
[17] Atanda, P.O., Akinlosotu, O.C. & Oluwole, O.O. (2014). Effect of some polysaccharide starch extracts on binding characteristics of foundry moulding sand. International Journal of Scientific & Engineering Research. 5(3), 362-367.
[18] Pezarski, F., Maniowski, Z., Izdebska-Szanda, I. & Smoluchowska, E. (2006). Investigations of moulding and core sands made with a new geopolymer binder assigned for production of steel castings. Archives of Foundry. 6(20), 65-70. (in Polish).
[19] Pezarski, F., Smoluchowska, E. & Izdebska-Szanda, I. (2008). Application of geopolymer binder in manufacturing of casting from ferrous alloys. Prace Instytutu Odlewnictwa. 48(2), 19-34. (in Polish).
[20] Jaworski, J. (2006). Research of stability of preparation system of circulating moulding sands. Archives of Foundry Engineering. 6(18), 495-500. (in Polish).
[21] Michta-Stawiarska, T. (2000). The selected iron castings defects as the effect of the sandmix quality. Solidification of Metais and Alloys. 2(43), 345-347. (in Polish).
[22] Lewandowski, J.L. (1971). Moulding materials. Warszawa Kraków: Wydawnictwo Naukowe PWN. (in Polish).
[23] Bobrowski, A. (2018). The phenomenon of dehydroxylation of selected mineral materials from the aluminosilicates group as the determinant factor of the knock-out improvement of moulding and core sands with inorganic binder. Wydawnictwo Archives of Foundry Engineering, Komisja Odlewnictwa PAN Katowice. (in Polish).
[24] Paduchowicz, P., Stachowicz, M. & Granat, K. (2017). Effect of Microwave Heating on Moulding Sand Properties with Gypsum Binder. Archives of Foundry Engineering. 17(3), 97-102.
[25] Sakwa, W., Wachelko, T. (1981). Foundry materials for molds and foundry cores. Katowice: Śląsk Publisher. (in Polish).
[26] Zhoua, X. , Yang J. & Quc. G. (2007). Study on synthesis and properties of modified starch binder for foundry. Journal of Materials Processing Technology. 183. 407-411.
[27] Aramide, F. O., Aribo, S. & Folorunso, D.O. (2011). Optimizing the moulding properties of recycled ilaro silica sand. Leonardo Journal of Sciences. 19, 93-102.
[28] Jordan, G., Eulenkamp, C., Calzada, E., Schillinger, B., Hoelzel, M., Gigler, A., Stanjek, H. & Schmahl, W.W. (2013). Quantitative in situ study of the dehydration of bentonite-bonded molding sands. Clays and Clay Minerals. 61(2), 133-140.
[29] Blaszkowski, K. (1975), Mold and core technology. Bielsko-Biała: WSiP. Wydanie III. (in Polish).
Go to article

Authors and Affiliations

B. Samociuk
1
ORCID: ORCID
B. Gal
1
D. Nowak
1
ORCID: ORCID

  1. Department of Foundry Engineering, Plastics and Automation, Wroclaw University of Technology, ul. Smoluchowskiego 25, 50-372 Wrocław, Poland
Download PDF Download RIS Download Bibtex

Abstract

In this research, the quality of manufactured cast metal-ceramic foams (manufactured using blowing gas) was tested. The causes responsible for defect formation in the composite foams and their consequences were analyzed using the FMEA (Failure Mode and Effects Analysis) method, which is a useful tool for minimizing losses caused by low product quality. This method involves analytically determining correlations between the cause and consequences of potential product defects, and it takes into account the criticality factor (risk). The FMEA analysis showed that pore breaks were the most "critical defect" (with the highest number of effects on the product, the Risk Priority Number, affecting the quality of the composite foam). The second most critical defect was discontinuities in the foam frame structure. Destruction or damage to the foam structure (although very rare) deprived the composite foam of its primary function, which is to reinforce the product. The third most critical defect was non-uniform foam pore size.
Go to article

Bibliography

[1] Duarte, I. & Ferreira, J.M.F. (2016). Composite and nanocomposite metal foams. Materials. 9(2), 79. DOI: 10.3390/ma9020079.
[2] Ashby, M.F., Evans, A.G., Fleck, N.A., Gibson, L.J., Hutchinson, J.W., Wadley, H.N.G. (2000). Metal Foams. A Design Guide. (1st ed.). Woburn, MA, USA: Butterworth Heinemann.
[3] Marx, J., Portanova, M. & Rabiei A. (2019). Ballistic performance of composite metal foam against large caliber threats. Composite Structures 225, 111032. DOI: 10.1016/j.compstruct.2019.111032.
[4] Banhart, J. (2001). Manufacture, characterization and application of cellular metals and metal foams. Progress in Materials Science. 46(6), 559-632. DOI: 10.1016/S0079-6425(00)00002-5.
[5] Orbulov, I.N., Szlancsik, A., Kemény, A. & Kincses, D. (2020). Compressive mechanical properties of low-cost, aluminium matrix syntactic foams. Composites Part A: Applied Science and Manufacturing 135, 105923. DOI: 10.1016/j.compositesa.2020.105923.
[6] Bejger A., Chybowski L. & Gawdzińska K. (2018). Utilizing elastic waves of acoustic emission to assess the condition of spray nozzles in a marine diesel engine. Journal of Marine Engineering & Technology. 17(3), 153-159. DOI: 10.1080/20464177.2018.1492361.
[7] Chunhui, K., Liubiao C., Xianlin, W., Yuan, Z. & Junjie, W. (2018). Thermal conductivity of open cell aluminum foam and its application as advanced thermal storage unit at low temperature. Rare Metal Materials and Engineering. 47(4), 1049-1053. DOI: 10.1016/S1875-5372(18)30118-8.
[8] Banhart, J. & Seeliger, H.W. (2008). Aluminium foam sandwich panels: manufacture, metallurgy and applications. Advanced Engineering Materials. 10(9), 793-802. DOI: 10.1002/adem.200800091.
[9] Lehmhus, D., Weise, J., Szlancsik, A. & Orbulov, I.N. (2020. Fracture toughness of hollow glass microsphere-filled iron matrix syntactic foams. Materials. 13(11), 2566. DOI: 10.3390/ma13112566.
[10] Czarnecka-Komorowska, D., Grześkowiak, K., Popielarski, P., Barczewski, M., Gawdzińska, K. & Popławski, M. (2020). Polyethylene wax modified by organoclay bentonite used in the lost-wax casting process: processing−structure−property relationships. Materials. 13(10), 10. DOI: 10.3390/ma13102255.
[11] Przestacki, D., Majchrowski, R. & Marciniak-Podsadna, L. (2016). Experimental research of surface roughness and surface texture after laser cladding. Applied Surface Science. 388(A), 420-423. DOI: 10.1016/j.apsusc.2015.12.093.
[12] Zhou, J., Gao, Z., Cuitino, A.M. & Soboyejo, W.O. (2004). Effects of heat treatment on the compressive deformation behavior of open cell aluminum foams. Materials Science and Engineering A. 386(1-2), 118-128. DOI: 10.1016/ j.msea.2004.07.042.
[13] Yamada, Y., Shimojima, K., Sakaguchi, Y., Mabuchi, M., Nakamura, M. & Asahina, T. (2000). Effects of heat treatment on compressive properties of AZ91 Mg and SG91A Al foams with open-cell structure. Materials Science and Engineering A. 280(1), 225-228. DOI: 10.1016/S0921-5093(99)00671-1.
[14] Xia, X.C., Chen, X.W., Zhang, Z., Chen, X., Zhao, W.M., Liao, B. & Hur, B. (2013). Effects of porosity and pore size on the compressive properties of closed-cell Mg alloy foam. Journal of Magnesium and Alloys. 1(4), 330-335. DOI: 10.1016/j.jma.2013.11.006.
[15] García-Moreno, F. (2016). Commercial applications of metal foams: their properties and production. Materials. 9(2), 85. DOI: 10.3390/ma9020085.
[16] Banhart, J. (2013). Light-metal foams-history of innovation and technological challenges. Advanced Engineering Materials. 15(3), 82-111. DOI: 10.1002/adem.201200217.
[17] Neville, B.P. & Rabiei A. (2008). Composite metal foams processed through powder metallurgy. Materials and Design. 29(2), 388-396. DOI: 10.1016/j.matdes.2007.01.026.
[18] Fuganti, A., Lorenzi, L., Grønsund, A. & Langseth, M. (2000). Aluminum foam for automotive applications. Advanced Engineering Materials. 2(4), 200-204. Doi:10.1002/(SICI)1527-2648(200004)2:4<200::AID-ADEM200>3.0.CO;2-2.
[19] Bhattacharya, A., Calmidi, V.V. & Mahajan, R.L. (2002). Thermophysical properties of high porosity metal foams. International Journal of Heat and Mass Transfer. 45(5), 1017-1031. DOI: 10.1016/S0017-9310(01)00220-4.
[20] Miyoshi, T., Itoh M., Akiyama, S. & Kitahara A. (2000). ALPORAS Aluminum foam: production process, properties, and applications. Advanced Engineering Materials. 2(4), 179-183. DOI: 10.1002/(SICI)1527-2648(200004)2:4179:: AID-ADEM179>3.0.CO;2-G.
[21] Sereni, J.G. (2001). Magnetic systems: specific heat. in: Encyclopedia of Materials: Science and Technology. (4986-4993). Elsevier.
[22] Reay, D. (2013). Metal foams: fundamentals and applications. Applied Thermal Engineering. 61(2), 1. DOI: 10.1016/j.applthermaleng.2013.07.002.
[23] Businessinsider.com: million metal foam market analysis, (2017). Retrieved November 20, 2020, from https://markets.businessinsider.com/news/stocks/global-100-million-metal-foam-market-analysis-2017-1009247173
[24] Gawdzińska, K., Grabian, J., Szweycer, M. (2008). Patent No. 211439. Method of producing structural elements from foamed metals.
[25] Kaczyński, P., Ptak M & Gawdzińska, K. (2020). Energy absorption of cast metal and composite foams tested in extremely low and high-temperatures. Materials & Design. 196. DOI: 10.1016/j.matdes.2020.109114.
[26] Aczel, A.D. (2005). Statistics in management. Warszawa: PWN. (in Polish).
[27] Hamrol, A., Mantura W. (2006). Quality Management: Theory and practice (3rd ed.). Warszawa: PWN. (in Polish).
[28] Hamrol, A. (2007). Quality management with examples. Warszawa: PWN. (in Polish).
[29] Gawdzińska, K. (2018). Assessment of the quality of cast material-ceramic composite foams (in Polish). Archives of Foundry Engineering. Katowice–Gliwice: Komisja Odlewnictwa PAN.
[30] Sika, R., Rogalewicz, M., Popielarski, P., Czarnecka-Komorowska, D., Przestacki, D., Gawdzińska, K. & Szymański, P. (2020). Decision support system in the field of defects assessment in the metal matrix composites castings. Materials. 13(16), 3552. DOI: 10.3390/ma13163552.
[31] Gawdzińska, K. (2015). Study of metallic-ceramic composite foams with application of the computer tomograph. Metalurgija. 54 (4), 671-674.
[32] Sobczak, J. (1998). Metal monolithic and composite foams and gazars. A compendium of knowledge about metal cell structures used in modern technical design. Kraków: Instytut Odlewnictwa. (in Polish). [33] Babcsán, N., Leilmeier, D., Degischer, H.P., Flankl, H.J. (2003). In: J. Banhart, N.A. Fleck, A. Mortensen (Eds.) MetFoam 2003: Proceedings of the 3rd International Conference on Cellular Metals and Metal Foaming Technology (pp. 101-106). Berlin (Germany): MIT Pub.
Go to article

Authors and Affiliations

P. Popielarski
1
ORCID: ORCID
R. Sika
1
D. Czarnecka-Komorowska
1
ORCID: ORCID
P. Szymański
1
ORCID: ORCID
M. Rogalewicz
1
K. Gawdzińska
2
ORCID: ORCID

  1. Institute of Materials Technology, Poznan University of Technology Piotrowo 3, 61-138 Poznań, Poland
  2. Faculty of Marine Engineering, Maritime University of Szczecin, Willowa 2-4, 71-650 Szczecin, Poland
Download PDF Download RIS Download Bibtex

Abstract

Diesel engine components in the combustion chamber have been exposed to cyclic loadings under environmental effects, including high temperatures and corrosive fluids. Therefore, knowing the corrosion-fatigue behavior of materials is essential for designer engineers. In this article, pure fatigue and corrosion-fatigue behaviors of the piston aluminum alloy have been experimentally investigated. For such an objective, as-cast and pre-corrosive standard samples were tested by the rotary bending fatigue machine, under 4 stress levels. Some specimens were exposed to the corrosive fluid with 0.00235 % of the sulfuric acid for 100 and 200 hours. The results showed higher weight losses for 200 hours immersion times. As another result, it could be concluded that the lifetime decreased in pre-corrosive samples for both 100 and 200 hours of the immersion time, compared to that of as-cast specimens. However, such a lifetime reduction was more significant for 200 hours of the immersion time, especially within the high-cycle fatigue regime (or lower stress levels). Under high stress levels, both pre-corrosive sample types had almost similar behaviors. The field-emission scanning electron microscopy images of specimen fracture surfaces indicated that the brittle region of the fractured surface was larger for specimens after the 200 hours of corrosion-fatigue testing than the other specimen.
Go to article

Bibliography

[1] Li, Z., Li, Ch., Liu, Y., Yu, L., Guo, Q. & Li, H. (2016). Effect of heat treatment on microstructure and mechanical property of Ale10%Mg2Si alloy. Journal of Alloys and Compounds. 663, 16-19. DOI: http://dx.doi.org/10.1016/ j.jallcom.2015.12.128.
[2] Wang, M., Pang, J.C., Li, S.X. & Zhang, Z.F. (2017). Low-cycle fatigue properties and life prediction of Al-Si piston alloy at elevated temperature. Materials Science and Engineering A. 704, 480-492. DOI: http://dx.doi.org/ 10.1016/j.msea.2017.08.014.
[3] Azadi, M. (2017). Cyclic thermo-mechanical stress, strain and continuum damage behaviors in light alloys during fatigue lifetime considering heat treatment effect. International Journal of Fatigue. 99, 303-314. DOI: http://dx.doi.org/10.1016/j.ijfatigue.2016.12.001.
[4] Guerin, M., Alexis, J., Andrieu, E., Blanc, C. & Odemer, G. (2015). Corrosion-fatigue lifetime of Aluminum-Copper-Lithium alloy 2050 in chloride solution. Materials and Design 87, 681-69. DOI: http://dx.doi.org/10.1016/j.matdes. 2015.08.003.
[5] Chen, Y., Zhou, J., Liu, Ch. & Wang, F. (2017). Effect of pre-deformation on the pre-corrosion multiaxial fatigue behaviors of 2024-T4 aluminum alloy. International Journal of Fatigue. 108, 35-46. DOI: https://doi.org/10.1016/ j.ijfatigue.2017.11.008.
[6] Chen, Y., Liu, Ch., Zhou, J. & Wang, X. (2017). Multiaxial fatigue behaviors of 2024-T4 aluminum alloy under different corrosion conditions. International Journal of Fatigue. 98, 269-278. DOI: http://dx.doi.org/10.1016/j.ijfatigue. 2017.02.004.
[7] Chen, Y., Liu, Ch., Zhou, J. & Wang, F. (2019). Effect of alternate corrosion factors on multiaxial low-cycle fatigue life of 2024-T4 aluminum alloy. Journal of Alloys and Compounds. 772, 1-14. DOI: https://doi.org/10.1016/ j.jallcom.2018.08.282.
[8] Rodriguez, R.I., Jordon, J.B., Allison, P.G., Rushing, T. & Garcia, L. (2019). Corrosion effects on fatigue behavior of dissimilar friction stir welding of high-strength aluminum alloys. Material Science and Engineering. 742, 255-268. DOI: https://doi.org/10.1016/j.msea.2018.11.020.
[9] Mishra, R.K. (2020). Study the effect of pre-corrosion on mechanical properties and fatigue life of aluminum alloy 8011. Materials Today: Proceedings. 25(4), 602-609. DOI: https://doi.org/10.1016/j.matpr.2019.07.375.
[10] Azadi, M., Bahmanabadi, H., Gruen, F. & Winter, G. (2020). Evaluation of tensile and low-cycle fatigue properties at elevated temperatures in piston aluminum-silicon alloys with and without nano-clay-particles and heat treatment. Materials Science and Engineering A. 788, 139497. DOI: https://doi.org/10.1016/j.msea.2020.139497.
[11] Metallic materials-rotating bar bending fatigue testing. (2010). Standard No. ISO-1143, ISO International Standard.
[12] Aroo, H., Parast, M.S.A., Azadi, M. & Azadi, M. (2020). Investigation of effects of nano-particles, heat treatment process and acid amount on corrosion rate in piston aluminum alloy using regression analysis. 11th International Conference on Internal Combustion Engines and Oil, Tehran, Iran (in Persian).
[13] Azadi, M., Zolfaghari, M., Rezanezhad, S. & Azadi, M. (2018). Effects of SiO2 nano-particles on tribological and mechanical properties of aluminum matrix composites by different dispersion methods. Applied Physics A. 124(5), 377. DOI: https://doi.org/10.1007/s12540-019-00498-7
[14] Azadi, M. & Aroo, H. (2020). Temperature effect on creep and fracture behaviors of nano-SiO2-composite and alsi12cu3ni2mgfe aluminum alloy. International Journal of Engineering. 33(8), 1579-1589. DOI: 10.5829/ije. 2020.33.08b.16.
[15] Azadi, M. & Aroo, H. (2019). Creep properties and failure mechanisms of aluminum alloy and aluminum matrix silicon oxide nano-composite under working conditions in engine pistons. Material Research Express. 6, 115020. DOI: https://doi.org/10.1088/2053-1591/ab455f.
[16] Zainon, F., Rafezi Ahmad, K. & Daud, R. (2015). Effect of heat treatment on microstructure, hardness and wear of aluminum alloy 332. Applied Mechanics and Materials. 786, 18-22. DOI: 10.4028/www.scientific.net/AMM.786.18.
[17] Han, L., Sui, Y., Wang, Q., Wang, K. & Jiang, Y. (2017). Effects of Nd on microstructure and mechanical properties of cast Al-Si-Cu-Ni-Mg piston alloys. Journal of Alloys and Compounds. 695, 1566-1572. DOI: https://doi.org/10.1016/ S1003-6326(20)65333-X.
[18] Humbertjean, A. & Beck, T. (2013). Effect of the casting process on microstructure and lifetime of the Al-piston-alloy AlSi12Cu4Ni3 under thermo-mechanical fatigue with superimposed high-cycle fatigue loading. International Journal of Fatigue. 53, 67-74. DOI: 10.1016/j.ijfatigue. 2011.09.017.
[19] Mollaei, M. Azadi, M. Tavakoli, H. (2018). A parametric study on mechanical properties of aluminum-silicon/SiO2 nano-composites by a solid-liquid phase processing. Applied Physics A, 124, 504. https://doi.org/10.1007/s00339-018-1929-2
[20] Arab, M., Azadi, M. & Mirzaee, O. (2020). Effects of manufacturing parameters on the corrosion behavior of Al–B4C nanocomposites, Materials Chemistry and Physics, 253, 123259. DOI: https://doi.org/10.1016/j.matchemphys.2020.123259.
Go to article

Authors and Affiliations

M. Azadi
1
ORCID: ORCID
H. Aroo
1
M.. Azadi
1
M.S.A. Parast
1

  1. Semnan University, Iran
Download PDF Download RIS Download Bibtex

Abstract

The article focused primarily on comparing the achieved mechanical results for AlSi7Mg0.3Cu0.5Zr and AlSi7Mg0.3Cu0.5Zr0.15Ti experimental alloys. Experimental variants with the addition of Zr ≥ 0.05 wt. % demonstrated the ability of Zr to precipitate in the form of Al3Zr or AlSiZr intermetallic phases. Zr precipitated in the form of long smooth needles with split ends. When evaluating the thermal analyses, the repeated peak was observed already with the initial addition of Zr in the range of approximately 630 °C. It was interesting to observe the increased interaction with other intermetallic phases. EDX analysis confirmed that the individual phases are based on Cu, Mg but also Fe. Similar phenomena were observed in experimental alloys with a constant addition of Zr and a gradual increase in Ti by 0.1 wt. %. A significant change occurred in the amount of precipitated Zr phases. A more significant increase in mechanical properties after heat treatment of AlSi7Mg0.3Cu0.5Zr experimental alloys was observed mainly above the Zr content ≥ 0.15 wt. % Zr. The improvement of yield and tensile strength over the AlSi7Mg0.3Cu0.5 reference alloy after heat treatment was minimal, not exceeding 1 %. A more significant improvement after heat treatment occurred in modulus of elongation with an increase by 6 %, and in hardness with an increase by 7 %. The most significant drop occurred in ductility where a decrease by 31 % was observed compared to the reference alloy. AlSi7Mg0.3Cu0.5Zr0.15Ti experimental alloys, characterized by varying Ti content, achieved a more significant improvement. The improvement in tensile strength over the AlSi7Mg0.3Cu0.5 reference alloy after heat treatment was minimal, not exceeding 1 %. A more significant improvement after heat treatment occurred in modulus of elongation with an increase by 12 %, in hardness with an increase by 12 % and the most significant improvement occurred in yield strengthwith a value of 18 %. The most significant decrease also occurred in ductility where, compared to the reference alloy, the ductility drop was by up to 67 %.
Go to article

Bibliography

[1] Vončina, M., Medved, J., Kores, S., Xie, P., Cziegler, A. & Schumacher, P. (2018). Effect of molybdenum an zirconium on aluminium casting alloys. Livarski Vestnik. 68-78.
[2] Medved, J. & Kores, M.V.S. (2018). Development of innovative Al-Si-Mn-Mg alloys with hight mechanical properties. The Minerals, Metals & Materials Society. 373-380. DOI 10.1007/978-3-319-72284-9_50.
[3] Pisarek, B.P., Rapiejko, C., Szymczak, T. & Payniak, T. (2017). Effect of Alloy Additions on the Structure and Mechanical Properties of the AlSi7Mg0.3 Alloy. Archives of Foundry Engineering. 17(1),137-142. ISSN: 1897-3310.
[4] Mahmudi, R., Sepehrband, P. & Ghasemi, H.M. (2006). Improve properties of A319 aluminium casting alloy modified with Zr. Materials Letters. 2606-2610. DOI: 10.1016/j.matlet.2006.01.046
[5] Sepehrband, P., Mahmudi, R., Khomamizadeh, F. (2004). Effect of Zr addition on the aging behavior of A319 aluminium cast alloy. Scripta Materialia. 253-257. DOI: 10.1016/j.scriptamat.2004.10.025
[6] Rakhmonov, J., Timelli, G. & Bonollo, F. (2017) Characterization of the solidification path and microstructure of secondary Al-7Si-3Cu-0,3Mg alloy with Zr, V and Ni additions. Material characterization. ISSN:1044-5803.
[7] Krajewski, W., Geer, A., Buraś, J., Piwowarski, G. & Krajewski, P. (2019). New developments of hight-zinc Al-Zn-Cu-Mn cast alloys. Materialstoday Proceedings. 306-311. DOI: 10.1016/j.matpr.2018.10.410.
[8] Hermandez-Sandoval, J., Samuel, A.M. & Vatierra, F.H. (2016). Thermal analysis for detection of Zr-rich phases in Al-Si-Cu-Mg 354-type alloys. Journal of metalcasting. ISSN 1939-5981.
[9] Bolibruchova, D., Kuriš, M., Matejka, M., Major Gabryś, K., Vicen, M., (2020) Effect of Ti on selected properties of AlSi7Mg0.3Cu0.5 alloy with constant addition of Zr. Archives of Metalurgy and Materials. 66(1), 65-72. DOI: 10.24425/amm.2021.134760.

Go to article

Authors and Affiliations

M. Kuriš
1
D. Bolibruchova
1
M. Matejka
1
ORCID: ORCID
E. Kantoríková
1
ORCID: ORCID

  1. University of Zilina, Faculty of Mechanical Engineering, Department of Technological Engineering, Univerzitna 1, 010 26 Zilina, Slovak Republic
Download PDF Download RIS Download Bibtex

Abstract

In this work, the free vibration behaviour of A357 composite plate reinforced with dual particle size (DPS) (3 wt.% coarse + 3 wt.% fine, 4 wt.% coarse + 2 wt.% fine, and 2 wt.% coarse + 4 wt.% fine) SiC is evaluated using the finite element method. To this end, first-order shear deformation theory (FSDT) has been used. The equations of motion have been derived using Hamilton’s principle and the solution has been obtained through condensation technique. A thorough parametric study was conducted to understand the effect of reinforcement size and weight fraction, boundary conditions, aspect ratio and length-to-width ratio of plate geometry on natural frequencies of A357/DPS-SiC composite plates. Results reveal significant influence of all the above variables on natural frequency of the composite plates. In all the cases, A357 composite plate reinforced with 4 wt.% coarse and 2 wt.% fine SiC particles displayed the highest natural frequency owing to its higher elastic and rigidity modulus. Further, the natural frequencies increase with decrease in aspect ratio of the plate geometry. Natural frequency also decreases with increase in the number of free edges. Lastly, increasing the length-to-width ratio drastically improves the natural frequency of the plates.
Go to article

Bibliography

[1] Raju R. S. S., Panigrahi, M.K., Ganguly R.I., & Srinivasa Rao G. (2019). Tribological behaviour of al-1100-coconut shell ash (CSA) composite at elevated temperature, Tribology International. 129, 55-66.
[2] Bishop, J.E., & Kinra, V.K. (1995). Analysis of elastothermodynamic damping in particle-reinforced metal-matrix composites. Metallurgical and Materials Transactions A. 26(11), 2773-2783.
[3] Challer, R.S. (2003). Metal matrix composites, a smart choice for high damping materials. Journal of Alloys and Compounds. 355(1-2), 131-135.
[4] Ehsani, R., & Seyed Reihani, S.M. (2004). Aging behaviour and tensile properties of squeeze cast Al 6061/SiC metal matrix composites. Scientia Iranica. 11(4), 392-397.
[5] Zhang, J., Perez, R.J., Wong, C.R., & Lavernia, E.J. (1994). Effects of secondary phases on the damping behaviour of metals, alloys and metal matrix composites. Materials Science and Engineering: R: Reports. 13 (8), 325-389.
[6] Lavernia, E.J., Perez, R.J., & Zhang, J. (1995). Damping behavior of discontinuously reinforced ai alloy metal-matrix composites. Metallurgical and Materials Transactions A. 26 (11), 2803-2818.
[7] Wang, J., Li, Z., Fan, G., Pan, H., Chen, Z., & Zhang, D. (2012). Reinforcement with graphene nanosheets in aluminum matrix composites. Scripta Materialia. 66(8), 594-597.
[8] Qian, L. F., Batra, R. C., & Chen, L. M. (2004). Static and dynamic deformations of thick functionally graded elastic plates by using higher-order shear and normal deformable plate theory and meshless local Petrov–Galerkin method. Composites Part B: Engineering. 35(6-8), 685-697.
[9] Sharma, S.C., Krishna, M., & Narasimha Murthy, H.N. (2004). Studies on the effect of residual thermal stresses on thermal expansion and damping behaviour of Al6061/ALBITE MMCs. Adv. in Vibration Engg., 3(4), 320-331 (2004).
[10] Sastry, S., Krishna, M., & Uchil, J. (2001). A study on damping behaviour of aluminite particulate reinforced ZA-27 alloy metal matrix composites. Journal of Alloys and Compounds. 314(1-2), 268-274.
[11] Zhang, J., Perez, R.J., Wong, C.R., & Lavernia, E.J. (1994). Effects of secondary phases on the damping behaviour of metals, alloys and metal matrix composites. Materials Science and Engineering: R: Reports. 13(8), 325-389.
[12] James, D.W. (1969). High damping metals for engineering applications. Materials Science and Engineering. 4(1), 1-8.
[13] Zhang, J., Perez, R.J., & Lavernia, E.J. (1993). Documentation of damping capacity of metallic, ceramic and metal-matrix composite materials. Journal of Materials Science. 28(9), 2395-2404.
[14] Zhang, J., Perez, R.J., & Lavernia, E.J. (1994). Effect of SiC and graphite particulates on the damping behavior of metal matrix composites. Acta Metallurgica et Materialia. 42(2), 395-409.
[15] Kang, C.S., Maeda, K., Wang, K.J., & Wakashima, K. (1998). Dynamic Young's modulus and internal friction in particulate SiC Al composites. Acta Materialia, 46(4), 1209-1220.
[16] Zhang, J., Perez, R.J., Gupta, M., & Lavernia, E.J. (1993). Damping behavior of particulate reinforced 2519 Al metal matrix composites. Scripta Metallurgica et Materialia, 28(1), 91-96.
[17] Ersulu S.O., & Aydogdu M, Mechanical and Vibration analysis of Al/SiC composite plates. Ankara International Aerospace Conference AIAC-070 (2007).
[18] El-Kady, E. Y., Mahmoud, T. S., El-Betar, A. A., & Abdel-Aziz, M. (2012). Dynamic behaviour of Cast A356/Al2O3 aluminum metal matrix nano composites. Materials Sciences and Applications. 3(11), 815-820.
[19] Ravikanth Raju, P., & Venkat Reddy, R. (2018). Mechanical characterization and free vibration of composite laminated plates. International Journal of Mechanical Engineering and Technology (IJMET) 9(9), 186-191.
[20] Soleymani Shishvan, S., & Asghari, A. H. (2017). Effects of particle shape and size distribution on particle size-dependent flow strengthening in metal matrix composites. Scientia Iranica B, 24 (3), 1091-1099.
[21] Civalek, Ö., Numanoğlu, H. M., & Mercan, K. (2019). Finite element model and size dependent stability analysis of boron nitride and silicon carbide nanowires/nanotubes. Scientia Iranica, 26(4), 2079-2099.
[22] Khan, A.A., Naushad Alam, M., & Wajid, M. (2016). Finite element modelling for static and free vibration response of functionally graded beam. Latin American Journal of Solids and Structures, 13, 690-714.
[23] Zuo, H., Yang, Z., Chen, X., Xie, Y., & Zhang, X. (2014). Bending, free vibration and buckling analysis of functionally graded plates via wavelet finite element method. Computers, Materials and Continua (CMC), 44 (3), 167-204.
[24] An, X., Liu, Y., Huang, F., & Jia, Q. (2018). MPFEM modeling on the compaction of Al/SiC composite powders with core/shell structure. Powder Technol. DOI: 10.5772/IntechOpen.76563, pp. 21-43, (2018).
[25] Bozkurt, Y., & Ersoy, S. (2016). Determining the vibration behavior of metal matrix composite used in aerospace industry by FEM. Vibroengineering PROCEDIA, 9, 29-32.
[26] Santhosh, N., & Kempaiah, U. N. (2018). Vibration characterization of SiCp and fly ash dispersion strengthened aluminium 5083 composites. Journal of Aerospace Engineering & Technology. 7(3), 61-72.
[27] Kushwaha, P.K., & Vimal, J. (2014). Study of vibration analysis of laminated composite plates using FEM. International Journal of Advanced Mechanical Engineering. 4(6), 675-680.
[28] Alaneme, K.K., & Fajemisin, A.V. (2018). Evaluation of the damping behaviour of Al-Mg-Si alloy-based composites reinforced with steel, steel and graphite, and silicon carbide particulates. Engineering Science and Technology, an International Journal. 21(4), 798-805.
[29] Gholami, R., & Ansari, R. (2019). On the vibration of postbuckled functionally graded-carbon nanotube reinforced composite annular plates. Scientia Iranica, 26(6), 3857-3874.
[30] Vinyas, M., Sunny, K.K., Harursampath, D., Nguyen-Thoi, T., & Loja, M.A.R. (2019). Influence of interphase on the multi-physics coupled frequency of three-phase smart magneto-electro-elastic composite plates. Composite Structures. 226, 111254.
[31] Vinyas, M., Sandeep, A.S., Nguyen-Thoi, T., Ebrahimi, F., & Duc, D.N. (2019). A finite element-based assessment of free vibration behaviour of circular and annular magneto-electro-elastic plates using higher order shear deformation theory. Journal of Intelligent Material Systems and Structures. 30(16), 2478-2501.
[32] Vinyas, M., Nischith, G., Loja, M.A.R., Ebrahimi, F., & Duc, N.D. (2019). Numerical analysis of the vibration response of skew magneto-electro-elastic plates based on the higher-order shear deformation theory. Composite Structures. 214, 132-142.
[33] Avinash, L., Ram Prabhu, T., & Bontha, S. (2016). The Effect on the dry sliding wear behavior of gravity cast A357 reinforced with dual size silicon carbide particles. Applied Mechanics and Materials. 829, 83-89.
[34] Lakshmikanthan, A., Bontha, S., Krishna, M., Koppad, P. G., & Ramprabhu, T. (2019). Microstructure, mechanical and wear properties of the A357 composites reinforced with dual sized SiC particles. Journal of Alloys and Compounds.786, 570-580.
[35] Avinash Lakshmikanthan, T. Ram Prabhu, Udayagiri Sai Babu, Praveennath G. Koppad, Manoj Gupta, Munishamaiah Krishna , Srikanth Bontha (2020). The effect of heat treatment on the mechanical and tribological properties of dual size SiC reinforced A357 matrix composites. Journal of Materials Research and Technology. 9(3), May June 2020, 6434-6452
[36] Matweb.com.2020.Matweb-The Online Materials Information Resource.[online] Available at :< http://www.matweb.com/search/DataSheet.aspx?
[37] Mahesh, V., Sagar, P. J., & Kattimani, S. (2018). Influence of coupled fields on free vibration and static behavior of functionally graded magneto-electro-thermo-elastic plate. Journal of Intelligent Material Systems and Structures. 29 (7), 1430-1455.
[38] Herrmann, J., Kühn, T., Müllenstedt, T., Mittelstedt, S., & Mittelstedt, C. (2018). Closed-form approximate solutions for the local buckling behaviour of composite laminated beams based on third order shear deformation theory. Advances in Mechanics of Materials and Structural Analysis. 80, 175-205.
[39] Vinyas, M., Kattimani, S.C. (2018). Finite element evaluation of free vibration characteristics of magneto-electro-elastic plates in hygrothermal environment using higher order shear deformation theory. Composite Structures. 202, 1339-1352.
[40] Vinyas, M. (2018). A higher order free vibration analysis of Carbon Nanotube-reinforced Magneto-electro-elastic plates using finite element methods. Composites Part-B. 158, 286-301.
[41] Mohammadimehr, M., Okhravi, S.V. & Akhavan Alavi, S.M. (2018). Free vibration analysis of magneto-electro-elastic cylindrical composite panel reinforced by various distributions of CNTs with considering open and closed circuits boundary conditions based on FSDT. Journal of Vibration and Control. 24(8), 1551-1569.
[42] Shen, H.S. (2009). Nonlinear bending of functionally graded carbon nanotube-reinforced composite plates in thermal environments. Composite Structures. 91, 9-19.
[43] Klimenda, F., & Soukup, J. (2017). Modal analysis of thin aluminium plate. Procedia Engineering. 177, 11-16.
Go to article

Authors and Affiliations

A. Lakshmikanthan
1 2
V. Mahesh
3
ORCID: ORCID
R.T. Prabhu
4
M.G.C. Patel
5
S. Bontha

  1. Department of Mechanical Engineering, National Institute of Technology Karnataka, Surathkal, Mangalore-575025, Karnataka, India
  2. Department of Mechanical Engineering, Nitte Meenakshi Institute of Technology, Bangalore, India-560064
  3. Nonlinear Multifunctional Composites Analysis and Design (NMCAD) Laboratory, Department of Aerospace Engineering, Indian Institute of Science, Bangalore, India-560012
  4. CEMILAC, Defence R&D Organisation, Bangalore, India-560093
  5. Department of Mechanical Engineering, PES Institute of Technology and Management, Shivamogga, India-577204
Download PDF Download RIS Download Bibtex

Abstract

The paper presents results of influence microwave drying on strength and technological properties of molding sand with gypsum binder researches, which, immediately after making and after the natural initial setting in air for 1, 2 or 5 hours, was heated with 250 W microwave power for 3, 6, 9 and 12 min time periods. The test was carried out on a mass containing (% -wt.): 88% Grudzeń-Las quartz sand, 12% "Dolina Nidy" plaster gypsum and 6% water. The loss of moisture content during natural drying and then microwave drying was determined, significant from the point of view of using the mass with gypsum binder in the production of products, using an environmentally friendly technology without casting incompatibilities. Additionally, the compressive strength of the mass was measured. The influence of both drying methods on the binder crystallization process and the associated mass strength was demonstrated, especially in terms of the possibility of selecting parameters and / or intensifying a specific drying method for use in the technology of manufacturing molds and foundry cores.
Go to article

Bibliography

[1] Borkowska, M. & Smulikowski, K. (1973). Rock forming minerals. Warszawa: Wydawnictwa Geologiczne. (in Polish).
[2] Lopez-Beceiro J., Gracia-Fernandez C., Tarrio-Saavedra J., Gomez-Barreiro S. & Artiaga R. „Study of gypsum by PDSC”. Journal of Thermal Analysis and Calorimetry (2012) 109: 1177-1183.
[3] Balance of mineral resources management in Poland and the world. Polish Geological Institute, Research Institute. Warszawa 2014. (in Polish)
[4] Chłądzyński, S. & Pichniarczyk, P. (2006). Gypsum and gypsum products in European standards. Materiały Budowlane. 6(10), 42-46. (in Polish).
[5] Akerman, K. (1964). Gypsum and anhydrite. Warszawa: PWN. (in Polish).
[6] Hazzat M., Sifou A., Ansalane S. & Hamidi A. (2019). Novel approach to termal degradation kinetics of gypsum: application of peak deconvolution and Model-Free isoconversional method. Journal of Thermal Analysis and Calorimetry. 140 (2).
[7] Badens E., Veesler S., Bojstelle R. (1999). Crystallization of gypsum from hemihydrate in presence of additives. Journal of Crystal Growth. 198-199. P. 704-709.
[8] Singh N.B., Middendorf B. (2007). Calcium sulphate hemihydrate hydratation leading to gypsum crystallization. Progress in Crystal Growth and Characterization of Materials. (53)7. 57-77.
[9] Pigiel M. & Granat K. (1997). Application of microwave heating in foundry. Krzepnięcie Metali i Stopów. 33/35. (in Polish).
[10] Parosa R. & Reszke E. (2000). Application of the microwave technique in foundry. Krzepnięcie Metali i Stopów. 2(2000), 419-425. (in Polish).
[11] Pawlak M. (2010). The influence of composition of gypsum plaster on its technological properties. Archives of Foundry Engineering. 10(4/2010), 55-60.
[12] Granat K., Paduchowicz P., Dziedzic A., Jamka M. & Biały P. (2020). Impact of hardening methods on the moulding sand’s properties with gypsum binder. Archives of Foundry Engineering. 4(20). 13-17. doi: 10.24425/afe.2020.133342.
[13] Nowak D., Gal B., Włodarska A. & Granat K. (2019). The influence of microwave drying parameters on the properties of synthetic moulding sands. Archives of Foundry Engineering. 4(19). 51-54.
[14] Gupta M. & Leong W. W. (2007). Microwaves and etals. Wiley. Azja 2007.
[15] Kowalski S., Rajewska K. & Rybicki A. Fizyczne podstawy suszenia mikrofalowego. Poznań: Wydawnictwo Politechniki Poznańskiej 2005 (in Polish).
[16] Kaczmarska K., Grabowska B. & Drożyński D. (2014). Analysis of selected properties of microwave-hardened molding sands bound with starch-based binders. Archives of Foundry Engineering. 4(14). 51-54. (in Polish).
[17] Banaszak J. & Rajewska K. (2013). Microwave drying of ceramic masses. Materiały odlewnicze. 2(2013), 180-185. (in Polish).
[18] Biały P. (2019). Selection of the method for curing environment-friendly moulding sands with a gypsum binder. Unpublished master thesis, Wroclaw University of Science and Technology, Wrocław, Poland. (in Polish).
[19] Zhenjun W., Nan D., Xiaofeng W. & Jie Z. (2020). Laboratory investigation of effects of microwave heating on early strength of cement bitumen emulsion mixture. Construction and Building Materials. 236(20). doi: 10.1016/j.conbuildmat.2019.117439
[20] Jinxin H., Guang X., Yunpei L., Guozung H. & Ping C. (2020). “Improving coal permeability using microwave heating technology – A rewiev”. Fuel. 266(2020). 10.1016/j.fuel.2020.117022
[21] Chaouki J., Farag S., Attia M. & Doucet J. (2020). The development of industrial (thermal) processes in the context of sustainability: The case of microwave heating. The Canadian Journal of Chemical Engineering. 98(2020). 832-847.
[22] Gajmal S. & Raut D.N. (2019). A review of opportunities and challenges in microwave assisted casting. Recent Trends i Production Engineering. 2(2019). 1-17.
[23] Paduchowicz P., Stachowicz M., Baszczuk A., Hasiak M. & Granat K. (2020). Evaluation of the chemical composition, TG – DTA and tensile strength tests of commercial gypsum kinds for foundry sandmixes application. Archives of Foundry Engineering. 2(20), 59-64.
[24] Dolina Nidy company catalog (2013 Juli). Technical data sheet. Retrieved Januar 7, 2016, from http://www.dolinanidy.com.pl/images/stories/pdf/gb.pdf
[25] Lewandowski J. L. (1997). Materials for foundry mass. Kraków: Akapit. (in Polish).
[26] Blajerska, P. (2016). Determination of the possible applicability of microwave in production of casting plaster mould. Unpublished master thesis, Wroclaw University of Science and Technology, Wrocław, Poland. (in Polish).
[27] Paduchowicz P, Stachowicz M. & Granat K. (2017). Effect of microwave heating on moulding sand properties with gypsum binder. Archives of Foundry Engineering. 3(2017), 97-102.
[28] PN-83 / H-11070
[29] PN-83/H-11073

Go to article

Authors and Affiliations

P.J. Paduchowicz
1
K. Granat
1
P. Biały
1

  1. Department of Foundry Engineering, Plastics and Automation, Wroclaw University of Technology, ul. Smoluchowskiego 25, 50-372 Wrocław, Poland
Download PDF Download RIS Download Bibtex

Abstract

The austenitic stainless steels are a group of alloys normally used under high mechanical and thermal requests, in which high temperature oxidation is normally present due to oxygen presence. This study examines the oxide layer evolution for Fe24Cr12NiXNb modified austenitic stainless steel A297 HH with 0,09%Nb and 0,77%Nb content at 900°C under atmospheric air and isothermal oxidation. The modifiers elements such as Mo, Co and Ti, added to provide high mechanical strength, varied due to the casting procedure, however main elements such as Cr, Ni, Mn and Si were kept at balanced levels to avoid microstructure changing. The oxide layer analysis was performed by confocal laser scanning microscopy (CLS) and scanning electron microscopy (SEM). The elemental analysis of the different phases was measured with energy dispersive X-ray spectroscopy (EDX). The Nb-alloyed steel generated a thicker Cr oxide layer. Generally elemental Nb did not provide any noticeable difference in oxide scale growth, for the specific range of Nb amount and temperature studied. High temperature oxidation up to 120h was characterized by protective Cr oxidation, after this period a non-protective Fe-based oxidation took place. Cr, Fe and Ni oxides were observed in the multilayer oxide scale.
Go to article

Bibliography

[1] Abbasi, M., Park, I., Ro, Y., Ji, Y., Ayer, R. & Shim, J.H. (2019). G-phase formation in twenty-years aged heat-resistant cast austenitic steel reformer tube. Materials Characterization. 148, 297-306. DOI: 10.1016/j.matchar. 2019.01.003.
[2] Madern, N., Monnier, J., Baddour-Hadjean, R., Steckmeyer, A. & Joubert, J.M. (2018). Characterization of refractory steel oxidation at high temperature. Corrosion Science. 132, 223-233. DOI: 10.1016/j.corsci.2017.12.029.
[3] Kondrat’ev, S.Y., Kraposhin, V.S., Anastasiadi, G.P. & Talis, A.L. (2015). Experimental observation and crystallographic description of M7C3 carbide transformation in Fe-Cr-Ni-C HP type alloy. Acta Materialia. 100, 275-281. DOI: 10.1016/j.actamat.2015.08.056.
[4] Dewar, M.P. & Gerlich, A.P. (2013). Correlation between experimental and calculated phase fractions in aged 20Cr32Ni1Nb austenitic stainless steels containing nitrogen . Metallurgical and Materials Transactions A. 44, 627-639. DOI: 10.1007/s11661-012-1457-1.
[5] Pascal, C., Braccini, M., Parry, V., Fedorova, E., Mantel, M., Oquab, D. & Monceau, D. (2017). Relation between microstructure induced by oxidation and room-temperature mechanical properties of the thermally grown oxide scales on austenitic stainless steels. Materials Characterization. 127, 161-170. DOI: 10.1016/j.matchar.2017.03.003.
[6] Chen, H., Wang, H., Sun, Q., Long, C., Wei, T., Kim, S.H., Chen, J., Kim, C., & Jang, C. (2018). Oxidation behavior of Fe-20Cr-25Ni-Nb austenitic stainless steel in high-temperature environment with small amount of water vapor. Corrosion Science. 145, 90-99. DOI: 10.1016/j.corsci. 2018.09.016.
[7] Zhang, X., Li, D., Li, Y. & Lu, S. (2019). Effect of aging treatment on the microstructures and mechanical properties evolution of 25Cr-20Ni austenitic stainless steel weldments with different Nb contents. Journal of Materials Science & Technology. 35, 520-529. DOI: 10.1016/j.jmst.2018.10.017.
[8] Birks, N., Meier, G.H. & Pettit, F.S. (2006). Introduction to the high temperature oxidation of metals, Second edition. Cambridge University Press. DOI: 10.1017/ CBO9781139163903.
[9] Li, D.S., Dai, Q.X., Cheng, X.N., Wang, R.R. & Huang, Y. (2012). High-temperature oxidation resistance of austenitic stainless steel Cr18Ni11Cu3Al3MnNb. Journal of Iron Steel Research International. 19, 74-78. DOI: 10.1016/S1006-706X(12)60103-4.
[10] Kaya, A.A. (2002). Microstructure of HK40 alloy after high-temperature service in oxidizing/carburizing environment: II. Carburization and carbide transformations. Materials Characterization. 49, 23-34. DOI: 10.1016/S1044-5803(02)00284-X.
[11] Li, H., Zhang, B., Jiang, Z., Zhang, S., Feng, H., Han, P., Dong, N., Zhang, W., Li, G., Fan, G. & Lin, Q. (2016). A new insight into high-temperature oxidation mechanism of super-austenitic stainless steel S32654 in air. Journal of Alloys and Compounds. 686, 326-338. DOI: 10.1016/j.jallcom.2016.06.023.
[12] M. Salehi Doolabi, B. Ghasemi, S.K. Sadrnezhaad, A. Feizabadi, A. HabibollahZadeh, D. Salehi Doolabi, M. AsadiZarch. (2017). Comparison of Isothermal with cyclic oxidation behavior of “Cr-Aluminide” coating on inconel 738LC at 900 °C. Oxidation of Metals. 87, 57-74. DOI: 10.1007/s11085-016-9657-5.
[13] De Almeida, L.H., Ribeiro, A.F. & Le May, I. (2002). Microstructural characterization of modified 25Cr-35Ni centrifugally cast steel furnace tubes. Materials Characterization. 49, 219-229. DOI: 10.1016/S1044-5803(03)00013-5.
[14] Nishimoto, K., Saida, K., Inui, M. & Takahashi, M. (2001). Changes in microstructure of HP-modified, heat-resisting cast alloys under long-term aging. Repair weld cracking of service-exposed, HP-modified, heat-resisting cast alloys (2nd report). Welding International. 15(7), 509-517. DOI: 10.1080/ 09507110109549397.
[15] Joubert, J.M., St-Fleur, W., Sarthou, J., Steckmeyer, A. & Fournier, B. (2014). Equilibrium characterization and thermodynamic calculations on highly alloyed refractory steels. Calphad Comput. Coupling Phase Diagrams Thermochem. 46, 55-61. DOI: 10.1016/j.calphad. 2014.02.002.
[16] Ramos, P.A., Coelho, R.S., Pinto, H.C., Soldera, F., Mücklich, F. & Brito, P. (2021). Microstructure and cyclic oxidation behavior of modified Nb-alloyed A297 HH refractory austenitic stainless steel. Materials Chemistry and Physics. 263, 124361. DOI: 10.1016/j.matchemphys. 2021.124361.
[17] Ramos, P.A., Coelho, R.S., Soldera, F., Pinto, H.C., Mücklich, F. & Brito,P. (2020). Residual stress analysis in thermally grown oxide scales developed on Nb-alloyed refractory austenitic stainless steels. Corrosion Science. 178, 109066. DOI: 10.1016/j.corsci.2020.109066.
[18] McCafferty E. (2010). Introduction to corrosion science. Springer Science & Business Media. DOI: 10.1007/978-1-4419-0455-3.

Go to article

Authors and Affiliations

P.A. Ramos
1 2
R.S. Coelho
3
H.C. Pinto
4
F. Soldera
5
F. Mücklich
5
P.P. Brito
1

  1. Pontifical Catholic University of Minas Gerais, Brazil
  2. Federal Institute of Science and Technology of Minas Gerais, Brazil
  3. SENAI CIMATEC, Institute of Innovation for Forming and Joining of Materials, Av. Orlando Gomes, 1845, Piatã, 41650-010, Salvador-BA, Brazil
  4. Department of Materials Engineering - SMM, São Carlos School of Engineering – EESC, University of São Paulo – USP, São Carlos, SP, Brazil
  5. Chair of Functional Materials, Department of Materials Science, Saarland University, 66123, Saarbrücken, Saarland, Germany
Download PDF Download RIS Download Bibtex

Abstract

The article describes the design of a proven technology for the production of metal foam and porous metal by the foundry. Porous metal formed by infiltrating liquid metal into a mould cavity appears to be the fastest and most economical method. However, even here we cannot do without the right production parameters. Based on the research, the production process was optimised and subsequently a functional sample of metal foam with an irregular internal structure - a filter - was produced. The copper alloy filter was cast into a gypsum mould using an evaporable model.
Furthermore, a functional sample of porous metal with a regular internal structure was produced - a heat exchanger. The aluminium alloy heat exchanger was cast into a green sand mould using preforms. Also, a porous metal casting with a regular internal structure was formed for use as an element in deformation zones. This aluminium alloy casting was made by the Lost Foam method. The aim is therefore to ensure the production of healthy castings, which would find use in the field of filtration of liquid metal or flue gases, in vehicles in the field of shock energy absorption and also in energy as a heat exchanger.
Go to article

Bibliography

[1] Lefebvre, L.P., Banhart, J. & Dunand, D. (2008). Porous metals and metallic foams: current status and recent developments. Advanced Engineering Materials. 10(9), 775-787.
[2] Banhart, J. (2001). Manufacture, characterisation and application of cellular metals and metal foams. Progress in Materials Science. 46(6), 559-632.
[3] Banhart, J. (2007). Metal Foams - from Fundamental Research to Applications [online], URL: < https://www.helmholtz-berlin.de/media/media/spezial/people/banhart/html/B-Conferences/b097_banhart2007.pdf>.
[4] Gaillard, Y., Dairon, J., & Fleuriot, M. (2011). Porous materials: innovations with many uses. Slévárenství. 11-12, roč. LIX, 374-378. (in Czech).
[5] Banhart, J. (2005). Aluminium foams for lighter vehicles. International Journal of Vehicle Design. 37, Nos. 2/3, 114-125. [online]. URL: < http://www.helmholtz-berlin.de/media/media/spezial/people/banhart/html/A-Journals/open/article/a082_banhart2005.pdf>.
[6] García-Moreno, F. Commercial Applications of Metal Foams: Their Properties and Production. [online]. URL: < http://www.mdpi.com/1996-1944/9/2/85/html>.
[7] Banhart, J. Metallic Foams II: properties and application [online]. URL: < http://materialsknowledge.org/docs/ Banhart-talk2.pdf>.
[8] Landolsi, M.W. (2016). Metal foam - an innovative material. [online]. URL: < https://conceptec.net/actualites/innovations/ 111-mousse-metallique-un-materiau-innovant>. (in Czech).
[9] Lulusoso. Composite cladding panel manufacturers [online]. URL: < http://www.lulusoso.com/products/ Composite-Cladding-Panel-Manufacturers.html>.
[10] Erg Materials and Aerospace; Duocel® Foam Cells. [online]. URL: < http://www.ergaerospace.com/products/ fuel-cells.html>.
[11] Kroupová, I., Lichý, P., Ličev, L., Hendrych, J. & Souček, K. (2018). Evaluation of properties of cast metal foams with irregular inner structure. Archives of Metallurgy and Materials. 63(4), 1845-1849. ISSN 1733-3490.
[12] Kroupova, I., Bednarova, V., Elbel, T. & Radkovsky, F. (2014). Proposal of method of removal of mould material from the fine structure of metallic foams used as filters. Archives of Metallurgy and Materials. 59(2), 727-730. ISSN 1733-3490.
[13] Yamada. Y., Shimojima, K., Sakaguchi, Y., Mabuchi, M., Nakamura, M., Asahina, T., Mukai, T., Kanahashi, H. & Higashi, K. (2000). Effects of heat treatment on compressive properties of AZ91 Mg and SG91A Al foams with open-cell structure. Materials Science and Engineering: A. 280(1), 225-228. DOI: https://doi.org/ 10.1016/S0921-5093(99)00671-1.
[14] Gawdzinska, K., Chybowski, L. & Przetakiewicz, W. (2017). Study of thermal properties of cast metal-ceramic composite foams. Archives of Metallurgy and Materials. 17(4), 47-50. ISSN 1897-3310.
[15] Haack, P.D., Butcher, R.P., Kim, T. & Lu, J.T. (2001). Novel lightweight metal foam heat exchangers. porvair fuel cell technology, Inc., Department of Engineering, University of Cambridge. January, [online]. URL: < https://www.researchgate.net/publication/267721239_Novel_Lightweight_Metal_Foam_Heat_Exchangers>.
[16] Radkovský, F., Merta, V. (2020). Use of numerical simulation in production of porous metal casting. Archives of Metallurgy and Materials. 54(2), 259-261. ISSN 1580-2949. DOI: 10.17222/mit.2019.145.
[17] Radkovský, F., Gebauer, M., Kroupová, I., Lichý, P. (2017). Metal foam as a heat exchanger. In METAL 2017, Conference proceedings, 26th Anniversary International Conference on Metallurgy and Materials, Tanger Ltd., Ostrava, 24. - 26. 5. 2017, Hotel Voroněž I, Brno.
[18] Lu, T.J., Stone, H.A. & Ashby, M.F. (1998). Heat transfer in open-cell metal foams. Acta Materialia. 46(10, 12) June, 3619-3635. DOI: https://doi.org/10.1016/S1359-6454(98) 00031-7
[19] Boomsma, K., Poulikakos, D. & Zwick, F. (2003). Metal foams as compact high performance heat exchangers. Mechanics of Materials, 35(12), 1161-1176. DOI: https://doi.org/10.1016/j.mechmat.2003.02.001.
[20] Hutter, C., Büchi, D., Zuber, V. & Rohr, R. (2011). Heat transfer in metal foams and designed porous media. Chemical Engineering Science. 66(17), 1 September 2011, 3806-3814. DOI: https://doi.org/10.1016/j.ces.2011.05.005
[21] Lichý, P., Elbel, T., Kroupová, I. & Radkovský, F. (2017). Preparation and evaluation of properties of cast metallic foams with regular inner structure. Archives of Metallurgy and Materials. 62(3), 1643-1646. ISSN 1733-3490. DOI: 10.1515/amm-2017-0251.
[22] Romanek, T. (2017). Manufacturing and Properties of Cast Metallic Foams with Regular Structure, Ostrava, Diploma thesis, VSB - Technical University of Ostrava, [online]. URL: http://www.ergaerospace.com/products/fuel-cells.htm>.
[23] Radkovský, F., Gebauer, M. & Merta, V. (2018). Optimizing of metal foam design for the use as a heat exchanger. Archives of Metallurgy and Materials. 63(4), 1875-1881. ISSN 1733-3490.

Go to article

Authors and Affiliations

F. Radkovský
1
ORCID: ORCID
V. Merta
1
ORCID: ORCID
T. Obzina
1

  1. VSB - Technical University of Ostrava, Czech Republic
Download PDF Download RIS Download Bibtex

Abstract

One of the main reason for decreased internal homogeneity of aluminium alloy castings is reoxidation. The resulting products of reoxidation are doubled oxides, so called "bifilms". Submitted paper deals with optimization of gating system design in order to reduce reoxidation processes taking place in mold cavity. Experimental work compares and evaluates three gating systems designs based on non-pressurized and naturally pressurized principles. Unconventional spin trap extension of runner was used in third design. Among the evaluated aspects were: mechanical properties, hot tearing index, visual inspection of average porosity amount, numerical simulation of velocity, turbulence and oxide amount. Paper aim is also to clarify the reoxidation phenomenon by visualization with the aid of ProCAST numerical simulation software. Results of mechanical properties and hot tear index clearly confirmed the positive effect of the naturally pressurized gating system with applied element for velocity reduction.
Go to article

Bibliography

[1] Svoboda, J.M., Monroe, R.W., Bates, C.E. & Griffin, J. (1987). TAFS. 95, 187-202.
[2] Campbell, J. (2006). Entrainment defects. Materials Science and Technology. 22(2), 127-145. ISSN 0267-0836. https://doi.org/10.1179/174328406X74248.
[3] Campbell, J. (1993). Invisible Macrodefects in castings. Journal de Physique Archives. 03(C7), 861-872. https://doi.org/10.1051/jp4:19937135.
[4] Dojka, R. Jezierski, J. & Campbell, J. (2018) Optimized gating system for steel castings. Journal of Materials Engineering and Performance. 10. DOI: 10.1007/s11665-018-3497-1.
[5] Sladek, A., Patek, M. & Mician, M. (2017). Behavior of steel branch connections during fatigue loading‎. Archives of Metallurgy and Materials. 62 (3), 1597-1601‏.
[6] Brůna, M., Bolibruchová, D. & Pastirčák, R. (2017). Archives of Foundry Engineering. 17, 23-26. https://doi.org/10.1515/afe-2017-0084.
[7] Lin, S., Aliravci, C. & Pekguleryuz, N.I.O. (2007). Hot-tear susceptibility of aluminum wrought alloys and the effect of grain refining. Materials Science and Engineering. A Sci. 38A, 1056-1068. https://doi.org/10.1007/s11661-007-9132-7.
[8] Campbell, J. (2006). An overview of the effects of bifilms on the structure and properties of cast alloys. Metallurgical and Materials Transaction B. 37, 857-863. https://doi.org/ 10.1007/BF0273500.

Go to article

Authors and Affiliations

M. Bruna
1
ORCID: ORCID
M. Galčík
1

  1. Department of Technological Engineering, University of Zilina, Univerzitna 1, 010 26 Zilina, Slovakia
Download PDF Download RIS Download Bibtex

Abstract

High tin bronze alloy (Cu>17wt.%Sn) is commonly as raw material to fabricate musical instruments. Gamelan musical instruments in Indonesia are produced using tin bronze alloy raw materials. The tin bronze alloy used by each gamelan craftsman has a different tin composition, generally in the range of Cu(20-24) wt.% Sn. This study aims to investigate the effect of microstructure, density, and mechanical properties of Cu(20-24)wt.%Sn against the acoustic properties processed by the sand casting method. The material is melted in a crucible furnace until it reaches a pouring temperature of 1100ºC by the sand casting method. The specimens were subjected to microstructure observations, density and porosity as well as mechanical properties testing including tensile strength, bending strength, hardness, and modulus of elasticity. Mechanical properties data then used to calculate several parameters of acoustic properties including speed of sound (c), impedance (z) and radiation coefficient (R). Processes simulation using Finite Element Analysis (FEA) and Experiment Method Analysis (EMA) were carried out to determine acoustic properties including sound intensity, natural frequency and damping capacity.
The experimental result shows that the increase in tin composition in Cu(20-24) wt.% Sn changed the microstructure of coarse grains into dendrite-columned fine grains. Physical properties of density decrease, while porosity increases. Mechanical properties including tensile strength, modulus of elasticity, and bending strength decreased, while the hardness of the alloy increases. The calculation of acoustic parameters such as the speed of sound (c), impedance (z) and radiation coefficient (R) has decreased. Moreover, sound intensity (dB), natural frequency (Hz) and damping capacity also decrease with increasing tin composition. Hence, tin bronze alloy Cu20wt.%Sn is the recommended raw material for the manufacture of gamelan instruments through the sand casting method.
Go to article

Bibliography

[1] Sumarsam. (2002). Introduction to Javanese gamelan (Javanese gamelan-beginners). Wesleyan University. Middletown.
[2] Sutton, R.A. (2007). Gamelan: The Traditional Sounds of Indonesia (review). Asian Music. 38(1), 142-144.
[3] Suyanto, Tjokronegoro H.A, Merthayasa I.G.N. & Supanggah R. (2015). Acoustic parameter for javanese gamelan performance in pendopo mangkunegaran Surakarta. Procedia – Social and Behavioral Sciences. 184. 322-327.
[4] Goodway, M. (1992). Metals of music. Materials Characterization. 29. 177-184.
[5] Audy, J. & Audy, K. (2008). Analysis of bell materials: Tin bronzes. China Foundry. 5(3). 199-204.
[6] Debut, V. Carvalho, M. Figueiredo, E. Antunes, J. & Silva, R. (2016). The sound of bronze: Virtual resurrection of a broken medieval bell. Journal of Cultural Heritage. 19. 544-554.
[7] Sugita, I.K.G. Soekrisno, R. Miasa, I.M. & Suyitno. (2011). Mechanical and damping properties of silicon bronze alloys for music applications. International Journal of Engineering &. Technology. 11(6). 81-85.
[8] Sugita, I.K.G. Soekrisno, R. & Miasa, I.M. (2011). The effect of annealing temperature on damping capacity of the bronze 20 % Sn alloy. International Journal of Mechanical & Mechatronics Engineering. IJMME-IJENS. 11(4).1-5.
[9] Slamet, S. Suyitno, & Kusumaningtyas, I. (2019). Effect of composition and pouring temperature of Cu (20-24) wt.% Sn by sand casting on fluidity and Mechanical Properties, Journal of Mechanical Engineering and Science. 13(4). 6022-6035.
[10] Sugita, I.K.G. & Miasa, I.M. (2013). Feasibility Study On The Use Of Silicon-Bronze Alloys As An Alternative Material For Balinese Musical Instruments. 20th International Congress on Sound & Vibration; 7-11 July 2013.1-5. Bangkok, Thailand
[11] Prayoga, B.T. Suyitno, Dharmastiti, R. & Akbar, F. (2018). Microstructural characterization, defect, and hardness of titanium femoral knee joint produced using vertical centrifugal investment casting. Journal of Mechanical Science and Technology.32(1).149-156.
[12] Salonitis, K. Jolly, M. & Zeng, B. (2017). Simulation-based energy and resource-efficient casting process chain selection : A case study. Procedia Manufacturing. 8. 67-74.
[13] Wegst, U.G. (2006). Wood For Sound. American Journal of Botany. 93.1439-1448.
[14] Adams, R. D. & Fox, M.A.O. (1973). Correlation of the damping capacity of cast iron with its mechanical properties and microstructure. Journal of Mechanical Engineering Science. 15(2). 81-94.
[15] Grafov, B.M. (1994). The archimedes law and electrocapillarity. Electrochimica Acta. 39. 467-469.
[16] ASTM. (2015). Standard test methods for bend testing of material for ductility.1.1-10.
[17] Sutiyoko & Suyitno. (2012). Effect of pouring temperature and casting thickness on fluidity, porosity and surface roughness in lost foam casting of gray cast iron. Procedia Engineering. 50. 88-94.
[18] Halvaee, A. & Talebi, A. (2001). Effect of process variables on microstructure and segregation in the centrifugal casting of C92200 alloy. Journal of Materials Processing Technology. 118, 123-127.
[19] Sutiyoko. Suyitno. & Mahardika. M. (2016). Effect of gating system on porosity and surface roughness of femoral stem in centrifugal casting. Adv. Sci. Technol. Soc. AIP Conference Proceedings. 1755, 1-6.
[20] Sulaiman, S. & Hamouda, A.M.S. (2004). Modeling and experimental investigation of the solidification process in sand casting. Journal of Materials Processing Technology. 156, 1723-1726.
[21] Nadolski, M. (2017). The Evaluation of Mechanical Properties of High-tin Bronzes. Archives of Foundry Engineering. 17(1), 127-130.
[22] Nimbulkar, S.L. & Dalu. R.S. (2016). Design optimization of gating and feeding system through simulation technique for sand casting of wear plate. Perspectives in Science. 8.39-42.
[23] Singh, R. & Singh, S. (2013). Effect of process parameters on surface hardness, dimensional accuracy, and surface roughness of investment cast components; Journal of Mechanical Science and Technology. 27(1), 191-197.
[24] Bartocha, D. & Baron, C. (2016). Influence of tin-bronze melting and pouring parameters on its properties and bells ’ tone. Archives of Foundry Engineering. 16(4), 17-22.

Go to article

Authors and Affiliations

S. Slamet
1 2
S. Suyitnoa
1
I. Kusumaningtyasa
1
I.M. Miasaa
1

  1. Universitas Gadjah Mada, Yogyakarta, Indonesia
  2. Universitas Muria Kudus, Kudus, Indonesia

Instructions for authors

Submission


To submit the article, please use the Editorial System provided here:

https://www.editorialsystem.com/afe


Papers submitted in any other way will not be accepted.



The Journal does not have submission charges.


The APC Article Processing Charge is 110 euros (500zł for Polish authors). In some cases, the APC is paid as a part of the scientific conference fee, for which the AFE journal is a supportive one. If not, it is payable after the acceptance of the final article by direct money transfer.


Bank account details:


Account holder: Stowarzyszenie Wychowankow Politechniki Slaskiej Kolo Odlewnikow
Account holder address: ul. Towarowa 7, 44-100 Gliwice, Poland
Account numbers: BIC BPKOPLPW IBAN PL17 1020 2401 0000 0202 0183 3748


Instructions for the preparation of an Archives of Foundry Engineering Paper

Publication Ethics Policy


Publication Ethics Policy

The standards of expected ethical behavior for all parties involved in publishing in the Archives of Foundry Engineering journal: the author, the journal editor and editorial board, the peer reviewers and the publisher are listed below.

All the articles submitted for publication in Archives of Foundry Engineering are peer reviewed for authenticity, ethical issues and usefulness as per Review Procedure document.

Duties of Editors
1. Monitoring the ethical standards: Editorial Board monitors the ethical standards of the submitted manuscripts and takes all possible measures against any publication malpractices.
2. Fair play: Submitted manuscripts are evaluated for their scientific content without regard to race, gender, sexual orientation, religious beliefs, citizenship, political ideology or any other issues that is a personal or human right.
3. Publication decisions: The Editor in Chief is responsible for deciding which of the submitted articles should or should not be published. The decision to accept or reject the article is based on its importance, originality, clarity, and its relevance to the scope of the journal and is made after the review process.
4. Confidentiality: The Editor in Chief and the members of the Editorial Board t ensure that all materials submitted to the journal remain confidential during the review process. They must not disclose any information about a submitted manuscript to anyone other than the parties involved in the publishing process i.e., authors, reviewers, potential reviewers, other editorial advisers, and the publisher.
5. Disclosure and conflict of interest: Unpublished materials disclosed in the submitted manuscript must not be used by the Editor and the Editorial Board in their own research without written consent of authors. Editors always precludes business needs from compromising intellectual and ethical standards.
6. Maintain the integrity of the academic record: The editors will guard the integrity of the published academic record by issuing corrections and retractions when needed and pursuing suspected or alleged research and publication misconduct. Plagiarism and fraudulent data is not acceptable. Editorial Board always be willing to publish corrections, clarifications, retractions and apologies when needed.

Retractions of the articles: the Editor in Chief will consider retracting a publication if:
- there are clear evidences that the findings are unreliable, either as a result of misconduct (e.g. data fabrication) or honest error (e.g. miscalculation or experimental error)
- the findings have previously been published elsewhere without proper cross-referencing, permission or justification (cases of redundant publication)
- it constitutes plagiarism or reports unethical research.
Notice of the retraction will be linked to the retracted article (by including the title and authors in the retraction heading), clearly identifies the retracted article and state who is retracting the article. Retraction notices should always mention the reason(s) for retraction to distinguish honest error from misconduct.
Retracted articles will not be removed from printed copies of the journal nor from electronic archives but their retracted status will be indicated as clearly as possible.

Duties of Authors
1. Reporting standards: Authors of original research should present an accurate account of the work performed as well as an objective discussion of its significance. Underlying data should be represented accurately in the paper. The paper should contain sufficient details and references to permit others to replicate the work. The fabrication of results and making of fraudulent or inaccurate statements constitute unethical behavior and will cause rejection or retraction of a manuscript or a published article.
2. Originality and plagiarism: Authors should ensure that they have written entirely original works, and if the authors have used the work and/or words of others they need to be cited or quoted. Plagiarism and fraudulent data is not acceptable.
3. Data access retention: Authors may be asked to provide the raw data for editorial review, should be prepared to provide public access to such data, and should be prepared to retain such data for a reasonable time after publication of their paper.
4. Multiple or concurrent publication: Authors should not in general publish a manuscript describing essentially the same research in more than one journal. Submitting the same manuscript to more than one journal concurrently constitutes unethical publishing behavior and is unacceptable.
5. Authorship of the manuscript: Authorship should be limited to those who have made a significant contribution to the conception, design, execution, or interpretation of the report study. All those who have made contributions should be listed as co-authors. The corresponding author should ensure that all appropriate co-authors and no inappropriate co-authors are included in the paper, and that all co-authors have seen and approved the final version of the paper and have agreed to its submission for publication.
6. Acknowledgement of sources: The proper acknowledgment of the work of others must always be given. The authors should cite publications that have been influential in determining the scope of the reported work.
7. Fundamental errors in published works: When the author discovers a significant error or inaccuracy in his/her own published work, it is the author’s obligation to promptly notify the journal editor or publisher and cooperate with the editor to retract or correct the paper.

Duties of Reviewers
1. Contribution to editorial decisions: Peer reviews assist the editor in making editorial decisions and may also help authors to improve their manuscript.
2. Promptness: Any selected reviewer who feels unqualified to review the research reported in a manuscript or knows that its timely review will be impossible should notify the editor and excuse himself/herself from the review process.
3. Confidentiality: All manuscript received for review must be treated as confidential documents. They must not be shown to or discussed with others except those authorized by the editor.
4. Standards of objectivity: Reviews should be conducted objectively. Personal criticism of the author is inappropriate. Reviewers should express their views clearly with appropriate supporting arguments.
5. Acknowledgement of sources: Reviewers should identify the relevant published work that has not been cited by authors. Any substantial similarity or overlap between the manuscript under consideration and any other published paper should be reported to the editor.
6. Disclosure and conflict of Interest: Privileged information or ideas obtained through peer review must be kept confidential and not used for personal advantage. Reviewers should not consider evaluating manuscripts in which they have conflicts of interest resulting from competitive, collaborative, or other relations with any of the authors, companies, or institutions involved in writing a paper.

Peer-review Procedure


Review Procedure


The Review Procedure for articles submitted to the Archives of Foundry Engineering agrees with the recommendations of the Ministry of Science and Higher Education published in a booklet: ‘Dobre praktyki w procedurach recenzyjnych w nauce’ (MNiSW, Dobre praktyki w procedurach recenzyjnych w nauce, Warszawa 2011).

Papers submitted to the Editorial System are primarily screened by editors with respect to scope, formal issues and used template. Texts with obvious errors (formatting other than requested, missing references, evidently low scientific quality) will be rejected at this stage or will be sent for the adjustments.

Once verified each article is checked by the anti-plagiarism system Cross Check powered by iThenticate®. After the positive response, the article is moved into: Initially verified manuscripts. When the similarity level is too high, the article will be rejected. There is no strict rule (i.e., percentage of the similarity), and it is always subject to the Editor’s decision.
Initially verified manuscripts are then sent to at least four independent referees outside the author’s institution and at least two of them outside of Poland, who:

have no conflict of interests with the author,
are not in professional relationships with the author,
are competent in a given discipline and have at least a doctorate degree and respective
scientific achievements,
have a good reputation as reviewers.


The review form is available online at the Journal’s Editorial System and contains the following sections:

1. Article number and title in the Editorial System

2. The statement of the Reviewer (to choose the right options):

I declare that I have not guessed the identity of the Author. I declare that I have guessed the identity of the Author, but there is no conflict of interest

3. Detailed evaluation of the manuscript against other researches published to this point:

Do you think that the paper title corresponds with its contents?
Yes No
Do you think that the abstract expresses the paper contents well?
Yes No
Are the results or methods presented in the paper novel?
Yes No
Do the author(s) state clearly what they have achieved?
Yes No
Do you find the terminology employed proper?
Yes No
Do you find the bibliography representative and up-to-date?
Yes No
Do you find all necessary illustrations and tables?
Yes No
Do you think that the paper will be of interest to the journal readers?
Yes No

4. Reviewer conclusion

Accept without changes
Accept after changes suggested by reviewer.
Rate manuscript once again after major changes and another review
Reject


5. Information for Editors (not visible for authors).

6. Information for Authors


Reviewing is carried out in the double blind process (authors and reviewers do not know each other’s names).

The appointed reviewers obtain summary of the text and it is his/her decision upon accepting/rejecting the paper for review within a given time period 21 days.

The reviewers are obliged to keep opinions about the paper confidential and to not use knowledge about it before publication.

The reviewers send their review to the Archives of Foundry Engineering by Editorial System. The review is archived in the system.

Editors do not accept reviews, which do not conform to merit and formal rules of scientific reviewing like short positive or negative remarks not supported by a close scrutiny or definitely critical reviews with positive final conclusion. The reviewer’s remarks are sent to the author. He/she has to consider all remarks and revise the text accordingly.

The author of the text has the right to comment on the conclusions in case he/she does not agree with them. He/she can request the article withdrawal at any step of the article processing.

The Editor-in-Chief (supported by members of the Editorial Board) decides on publication based on remarks and conclusions presented by the reviewers, author’s comments and the final version of the manuscript.

The final Editor’s decision can be as follows:
Accept without changes
Reject


The rules for acceptance or rejection of the paper and the review form are available on the Web page of the AFE publisher.

Once a year Editorial Office publishes present list of cooperating reviewers.
Reviewing is free of charge.
All articles, including those rejected and withdrawn, are archived in the Editorial System.

Reviewers

List of Reviewers 2022

Shailee Acharya - S. V. I. T Vasad, India
Vivek Ayar - Birla Vishvakarma Mahavidyalaya Vallabh Vidyanagar, India
Mohammad Azadi - Semnan University, Iran
Azwinur Azwinur - Politeknik Negeri Lhokseumawe, Indonesia
Czesław Baron - Silesian University of Technology, Gliwice, Poland
Dariusz Bartocha - Silesian University of Technology, Gliwice, Poland
Iwona Bednarczyk - Silesian University of Technology, Gliwice, Poland
Artur Bobrowski - AGH University of Science and Technology, Kraków
Poland Łukasz Bohdal - Koszalin University of Technology, Koszalin Poland
Danka Bolibruchova - University of Zilina, Slovak Republic
Joanna Borowiecka-Jamrozek- The Kielce University of Technology, Poland
Debashish Bose - Metso Outotec India Private Limited, Vadodara, India
Andriy Burbelko - AGH University of Science and Technology, Kraków
Poland Ganesh Chate - KLS Gogte Institute of Technology, India
Murat Çolak - Bayburt University, Turkey
Adam Cwudziński - Politechnika Częstochowska, Częstochowa, Poland
Derya Dispinar- Istanbul Technical University, Turkey
Rafał Dojka - ODLEWNIA RAFAMET Sp. z o. o., Kuźnia Raciborska, Poland
Anna Dolata - Silesian University of Technology, Gliwice, Poland
Tomasz Dyl - Gdynia Maritime University, Gdynia, Poland
Maciej Dyzia - Silesian University of Technology, Gliwice, Poland
Eray Erzi - Istanbul University, Turkey
Flora Faleschini - University of Padova, Italy
Imre Felde - Obuda University, Hungary
Róbert Findorák - Technical University of Košice, Slovak Republic
Aldona Garbacz-Klempka - AGH University of Science and Technology, Kraków, Poland
Katarzyna Gawdzińska - Maritime University of Szczecin, Poland
Marek Góral - Rzeszow University of Technology, Poland
Barbara Grzegorczyk - Silesian University of Technology, Gliwice, Poland
Grzegorz Gumienny - Technical University of Lodz, Poland
Ozen Gursoy - University of Padova, Italy
Gábor Gyarmati - University of Miskolc, Hungary
Jakub Hajkowski - Poznan University of Technology, Poland
Marek Hawryluk - Wroclaw University of Science and Technology, Poland
Aleš Herman - Czech Technical University in Prague, Czech Republic
Mariusz Holtzer - AGH University of Science and Technology, Kraków, Poland
Małgorzata Hosadyna-Kondracka - Łukasiewicz Research Network - Krakow Institute of Technology, Poland
Dario Iljkić - University of Rijeka, Croatia
Magdalena Jabłońska - Silesian University of Technology, Gliwice, Poland
Nalepa Jakub - Silesian University of Technology, Gliwice, Poland
Jarosław Jakubski - AGH University of Science and Technology, Kraków, Poland
Aneta Jakubus - Akademia im. Jakuba z Paradyża w Gorzowie Wielkopolskim, Poland
Łukasz Jamrozowicz - AGH University of Science and Technology, Kraków, Poland
Krzysztof Janerka - Silesian University of Technology, Gliwice, Poland
Karolina Kaczmarska - AGH University of Science and Technology, Kraków, Poland
Jadwiga Kamińska - Łukasiewicz Research Network – Krakow Institute of Technology, Poland
Justyna Kasinska - Kielce University Technology, Poland
Magdalena Kawalec - AGH University of Science and Technology, Kraków, Poland
Gholamreza Khalaj - Islamic Azad University, Saveh Branch, Iran
Angelika Kmita - AGH University of Science and Technology, Kraków, Poland
Marcin Kondracki - Silesian University of Technology, Gliwice Poland
Vitaliy Korendiy - Lviv Polytechnic National University, Lviv, Ukraine
Aleksandra Kozłowska - Silesian University of Technology, Gliwice, Poland
Ivana Kroupová - VSB - Technical University of Ostrava, Czech Republic
Malgorzata Lagiewka - Politechnika Czestochowska, Częstochowa, Poland
Janusz Lelito - AGH University of Science and Technology, Kraków, Poland
Jingkun Li - University of Science and Technology Beijing, China
Petr Lichy - Technical University Ostrava, Czech Republic
Y.C. Lin - Central South University, China
Mariusz Łucarz - AGH University of Science and Technology, Kraków, Poland
Ewa Majchrzak - Silesian University of Technology, Gliwice, Poland
Barnali Maji - NIT-Durgapur: National Institute of Technology, Durgapur, India
Pawel Malinowski - AGH University of Science and Technology, Kraków, Poland
Marek Matejka - University of Zilina, Slovak Republic
Bohdan Mochnacki - Technical University of Occupational Safety Management, Katowice, Poland
Grzegorz Moskal - Silesian University of Technology, Poland
Kostiantyn Mykhalenkov - National Academy of Science of Ukraine, Ukraine
Dawid Myszka - Silesian University of Technology, Gliwice, Poland
Maciej Nadolski - Czestochowa University of Technology, Poland
Krzysztof Naplocha - Wrocław University of Science and Technology, Poland
Daniel Nowak - Wrocław University of Science and Technology, Poland
Tomáš Obzina - VSB - Technical University of Ostrava, Czech Republic
Peiman Omranian Mohammadi - Shahid Bahonar University of Kerman, Iran
Zenon Opiekun - Politechnika Rzeszowska, Rzeszów, Poland
Onur Özbek - Duzce University, Turkey
Richard Pastirčák - University of Žilina, Slovak Republic
Miroslawa Pawlyta - Silesian University of Technology, Gliwice, Poland
Jacek Pezda - ATH Bielsko-Biała, Poland
Bogdan Piekarski - Zachodniopomorski Uniwersytet Technologiczny, Szczecin, Poland
Jacek Pieprzyca - Silesian University of Technology, Gliwice, Poland
Bogusław Pisarek - Politechnika Łódzka, Poland
Marcela Pokusová - Slovak Technical University in Bratislava, Slovak Republic
Hartmut Polzin - TU Bergakademie Freiberg, Germany
Cezary Rapiejko - Lodz University of Technology, Poland
Arron Rimmer - ADI Treatments, Doranda Way, West Bromwich, West Midlands, United Kingdom
Jaromír Roučka - Brno University of Technology, Czech Republic
Charnnarong Saikaew - Khon Kaen University Thailand Amit Sata - MEFGI, Faculty of Engineering, India
Mariola Saternus - Silesian University of Technology, Gliwice, Poland
Vasudev Shinde - DKTE' s Textile and Engineering India Robert Sika - Politechnika Poznańska, Poznań, Poland
Bozo Smoljan - University North Croatia, Croatia
Leszek Sowa - Politechnika Częstochowska, Częstochowa, Poland
Sławomir Spadło - Kielce University of Technology, Poland
Mateusz Stachowicz - Wroclaw University of Technology, Poland
Marcin Stawarz - Silesian University of Technology, Gliwice, Poland
Grzegorz Stradomski - Czestochowa University of Technology, Poland
Roland Suba - Schaeffler Skalica, spol. s r.o., Slovak Republic
Maciej Sułowski - AGH University of Science and Technology, Kraków, Poland
Jan Szajnar - Silesian University of Technology, Gliwice, Poland
Michal Szucki - TU Bergakademie Freiberg, Germany
Tomasz Szymczak - Lodz University of Technology, Poland
Damian Słota - Silesian University of Technology, Gliwice, Poland
Grzegorz Tęcza - AGH University of Science and Technology, Kraków, Poland
Marek Tkocz - Silesian University of Technology, Gliwice, Poland
Andrzej Trytek - Rzeszow University of Technology, Poland
Mirosław Tupaj - Rzeszow University of Technology, Poland
Robert B Tuttle - Western Michigan University United States Seyed Ebrahim Vahdat - Ayatollah Amoli Branch, Islamic Azad University, Amol, Iran
Iveta Vaskova - Technical University of Kosice, Slovak Republic
Dorota Wilk-Kołodziejczyk - AGH University of Science and Technology, Kraków, Poland
Ryszard Władysiak - Lodz University of Technology, Poland
Çağlar Yüksel - Atatürk University, Turkey
Renata Zapała - AGH University of Science and Technology, Kraków, Poland
Jerzy Zych - AGH University of Science and Technology, Kraków, Poland
Andrzej Zyska - Czestochowa University of Technology, Poland



List of Reviewers 2021

Czesław Baron - Silesian University of Technology, Gliwice, Poland
Imam Basori - State University of Jakarta, Indonesia
Leszek Blacha - Silesian University of Technology, Gliwice
Poland Artur Bobrowski - AGH University of Science and Technology, Kraków, Poland
Danka Bolibruchova - University of Zilina, Slovak Republic
Pedro Brito - Pontifical Catholic University of Minas Gerais, Brazil
Marek Bruna - University of Zilina, Slovak Republic
Marcin Brzeziński - AGH University of Science and Technology, Kraków, Poland
Andriy Burbelko - AGH University of Science and Technology, Kraków, Poland
Alexandros Charitos - TU Bergakademie Freiberg, Germany
Ganesh Chate - KLS Gogte Institute of Technology, India
L.Q. Chen - Northeastern University, China
Zhipei Chen - University of Technology, Netherlands
Józef Dańko - AGH University of Science and Technology, Kraków, Poland
Brij Dhindaw - Indian Institute of Technology Bhubaneswar, India
Derya Dispinar - Istanbul Technical University, Turkey
Rafał Dojka - ODLEWNIA RAFAMET Sp. z o. o., Kuźnia Raciborska, Poland
Anna Dolata - Silesian University of Technology, Gliwice, Poland
Agnieszka Dulska - Silesian University of Technology, Gliwice, Poland
Maciej Dyzia - Silesian University of Technology, Poland
Eray Erzi - Istanbul University, Turkey
Przemysław Fima - Institute of Metallurgy and Materials Science PAN, Kraków, Poland
Aldona Garbacz-Klempka - AGH University of Science and Technology, Kraków, Poland
Dipak Ghosh - Forace Polymers P Ltd., India
Beata Grabowska - AGH University of Science and Technology, Kraków, Poland
Adam Grajcar - Silesian University of Technology, Gliwice, Poland
Grzegorz Gumienny - Technical University of Lodz, Poland
Gábor Gyarmati - Foundry Institute, University of Miskolc, Hungary
Krzysztof Herbuś - Silesian University of Technology, Gliwice, Poland
Aleš Herman - Czech Technical University in Prague, Czech Republic
Mariusz Holtzer - AGH University of Science and Technology, Kraków, Poland
Małgorzata Hosadyna-Kondracka - Łukasiewicz Research Network - Krakow Institute of Technology, Kraków, Poland
Jarosław Jakubski - AGH University of Science and Technology, Kraków, Poland
Krzysztof Janerka - Silesian University of Technology, Gliwice, Poland
Robert Jasionowski - Maritime University of Szczecin, Poland
Agata Jażdżewska - Gdansk University of Technology, Poland
Jan Jezierski - Silesian University of Technology, Gliwice, Poland
Karolina Kaczmarska - AGH University of Science and Technology, Kraków, Poland
Jadwiga Kamińska - Centre of Casting Technology, Łukasiewicz Research Network – Krakow Institute of Technology, Poland
Adrian Kampa - Silesian University of Technology, Gliwice, Poland
Wojciech Kapturkiewicz- AGH University of Science and Technology, Kraków, Poland
Tatiana Karkoszka - Silesian University of Technology, Gliwice, Poland
Gholamreza Khalaj - Islamic Azad University, Saveh Branch, Iran
Himanshu Khandelwal - National Institute of Foundry & Forging Technology, Hatia, Ranchi, India
Angelika Kmita - AGH University of Science and Technology, Kraków, Poland
Grzegorz Kokot - Silesian University of Technology, Gliwice, Poland
Ladislav Kolařík - CTU in Prague, Czech Republic
Marcin Kondracki - Silesian University of Technology, Gliwice, Poland
Dariusz Kopyciński - AGH University of Science and Technology, Kraków, Poland
Janusz Kozana - AGH University of Science and Technology, Kraków, Poland
Tomasz Kozieł - AGH University of Science and Technology, Kraków, Poland
Aleksandra Kozłowska - Silesian University of Technology, Gliwice Poland
Halina Krawiec - AGH University of Science and Technology, Kraków, Poland
Ivana Kroupová - VSB - Technical University of Ostrava, Czech Republic
Wacław Kuś - Silesian University of Technology, Gliwice, Poland
Jacques Lacaze - University of Toulouse, France
Avinash Lakshmikanthan - Nitte Meenakshi Institute of Technology, India
Jaime Lazaro-Nebreda - Brunel Centre for Advanced Solidification Technology, Brunel University London, United Kingdom
Janusz Lelito - AGH University of Science and Technology, Kraków, Poland
Tomasz Lipiński - University of Warmia and Mazury in Olsztyn, Poland
Mariusz Łucarz - AGH University of Science and Technology, Kraków, Poland
Maria Maj - AGH University of Science and Technology, Kraków, Poland
Jerzy Mendakiewicz - Silesian University of Technology, Gliwice, Poland
Hanna Myalska-Głowacka - Silesian University of Technology, Gliwice, Poland
Kostiantyn Mykhalenkov - Physics-Technological Institute of Metals and Alloys, National Academy of Science of Ukraine, Ukraine
Dawid Myszka - Politechnika Warszawska, Warszawa, Poland
Maciej Nadolski - Czestochowa University of Technology, Poland
Daniel Nowak - Wrocław University of Science and Technology, Poland
Mitsuhiro Okayasu - Okayama University, Japan
Agung Pambudi - Sebelas Maret University in Indonesia, Indonesia
Richard Pastirčák - University of Žilina, Slovak Republic
Bogdan Piekarski - Zachodniopomorski Uniwersytet Technologiczny, Szczecin, Poland
Bogusław Pisarek - Politechnika Łódzka, Poland
Seyda Polat - Kocaeli University, Turkey
Hartmut Polzin - TU Bergakademie Freiberg, Germany
Alena Pribulova - Technical University of Košice, Slovak Republic
Cezary Rapiejko - Lodz University of Technology, Poland
Arron Rimmer - ADI Treatments, Doranda Way, West Bromwich West Midlands, United Kingdom
Iulian Riposan - Politehnica University of Bucharest, Romania
Ferdynand Romankiewicz - Uniwersytet Zielonogórski, Zielona Góra, Poland
Mario Rosso - Politecnico di Torino, Italy
Jaromír Roučka - Brno University of Technology, Czech Republic
Charnnarong Saikaew - Khon Kaen University, Thailand
Mariola Saternus - Silesian University of Technology, Gliwice, Poland
Karthik Shankar - Amrita Vishwa Vidyapeetham , Amritapuri, India
Vasudev Shinde - Shivaji University, Kolhapur, Rajwada, Ichalkaranji, India
Robert Sika - Politechnika Poznańska, Poznań, Poland
Jerzy Sobczak - AGH University of Science and Technology, Kraków, Poland
Sebastian Sobula - AGH University of Science and Technology, Kraków, Poland
Marek Soiński - Akademia im. Jakuba z Paradyża w Gorzowie Wielkopolskim, Poland
Mateusz Stachowicz - Wroclaw University of Technology, Poland
Marcin Stawarz - Silesian University of Technology, Gliwice, Poland
Andrzej Studnicki - Silesian University of Technology, Gliwice, Poland
Mayur Sutaria - Charotar University of Science and Technology, CHARUSAT, Gujarat, India
Maciej Sułowski - AGH University of Science and Technology, Kraków, Poland
Sutiyoko Sutiyoko - Manufacturing Polytechnic of Ceper, Klaten, Indonesia
Tomasz Szymczak - Lodz University of Technology, Poland
Marek Tkocz - Silesian University of Technology, Gliwice, Poland
Andrzej Trytek - Rzeszow University of Technology, Poland
Jacek Trzaska - Silesian University of Technology, Gliwice, Poland
Robert B Tuttle - Western Michigan University, United States
Muhammet Uludag - Selcuk University, Turkey
Seyed Ebrahim Vahdat - Ayatollah Amoli Branch, Islamic Azad University, Amol, Iran
Tomasz Wrobel - Silesian University of Technology, Gliwice, Poland
Ryszard Władysiak - Lodz University of Technology, Poland
Antonin Zadera - Brno University of Technology, Czech Republic
Renata Zapała - AGH University of Science and Technology, Kraków, Poland
Bo Zhang - Hunan University of Technology, China
Xiang Zhang - Wuhan University of Science and Technology, China
Eugeniusz Ziółkowski - AGH University of Science and Technology, Kraków, Poland
Sylwia Żymankowska-Kumon - AGH University of Science and Technology, Kraków, Poland
Andrzej Zyska - Czestochowa University of Technology, Poland



List of Reviewers 2020

Shailee Acharya - S. V. I. T Vasad, India
Mohammad Azadi - Semnan University, Iran
Rafał Babilas - Silesian University of Technology, Gliwice, Poland
Czesław Baron - Silesian University of Technology, Gliwice, Poland
Dariusz Bartocha - Silesian University of Technology, Gliwice, Poland
Emin Bayraktar - Supmeca/LISMMA-Paris, France
Jaroslav Beňo - VSB-Technical University of Ostrava, Czech Republic
Artur Bobrowski - AGH University of Science and Technology, Kraków, Poland
Grzegorz Boczkal - AGH University of Science and Technology, Kraków, Poland
Wojciech Borek - Silesian University of Technology, Gliwice, Poland
Pedro Brito - Pontifical Catholic University of Minas Gerais, Brazil
Marek Bruna - University of Žilina, Slovak Republic
John Campbell - University of Birmingham, United Kingdom
Ganesh Chate - Gogte Institute of Technology, India
L.Q. Chen - Northeastern University, China
Mirosław Cholewa - Silesian University of Technology, Gliwice, Poland
Khanh Dang - Hanoi University of Science and Technology, Viet Nam
Vladislav Deev - Wuhan Textile University, China
Brij Dhindaw - Indian Institute of Technology Bhubaneswar, India
Derya Dispinar - Istanbul Technical University, Turkey
Malwina Dojka - Silesian University of Technology, Gliwice, Poland
Rafał Dojka - ODLEWNIA RAFAMET Sp. z o. o., Kuźnia Raciborska, Poland
Anna Dolata - Silesian University of Technology, Gliwice, Poland
Agnieszka Dulska - Silesian University of Technology, Gliwice, Poland
Tomasz Dyl - Gdynia Maritime University, Poland
Maciej Dyzia - Silesian University of Technology, Gliwice, Poland
Eray Erzi - Istanbul University, Turkey
Katarzyna Gawdzińska - Maritime University of Szczecin, Poland
Sergii Gerasin - Pryazovskyi State Technical University, Ukraine
Dipak Ghosh - Forace Polymers Ltd, India
Marcin Górny - AGH University of Science and Technology, Kraków, Poland
Marcin Gołąbczak - Lodz University of Technology, Poland
Beata Grabowska - AGH University of Science and Technology, Kraków, Poland
Adam Grajcar - Silesian University of Technology, Gliwice, Poland
Grzegorz Gumienny - Technical University of Lodz, Poland
Libor Hlavac - VSB Ostrava, Czech Republic
Mariusz Holtzer - AGH University of Science and Technology, Kraków, Poland
Philippe Jacquet - ECAM, Lyon, France
Jarosław Jakubski - AGH University of Science and Technology, Kraków, Poland
Damian Janicki - Silesian University of Technology, Gliwice, Poland
Witold Janik - Silesian University of Technology, Gliwice, Poland
Robert Jasionowski - Maritime University of Szczecin, Poland
Jan Jezierski - Silesian University of Technology, Gliwice, Poland
Jadwiga Kamińska - Łukasiewicz Research Network – Krakow Institute of Technology, Poland
Justyna Kasinska - Kielce University Technology, Poland
Magdalena Kawalec - Akademia Górniczo-Hutnicza, Kraków, Poland
Angelika Kmita - AGH University of Science and Technology, Kraków, Poland
Ladislav Kolařík -Institute of Engineering Technology CTU in Prague, Czech Republic
Marcin Kondracki - Silesian University of Technology, Gliwice, Poland
Sergey Konovalov - Samara National Research University, Russia
Aleksandra Kozłowska - Silesian University of Technology, Gliwice, Poland
Janusz Krawczyk - AGH University of Science and Technology, Kraków, Poland
Halina Krawiec - AGH University of Science and Technology, Kraków, Poland
Ivana Kroupová - VSB - Technical University of Ostrava, Czech Republic
Agnieszka Kupiec-Sobczak - Cracow University of Technology, Poland
Tomasz Lipiński - University of Warmia and Mazury in Olsztyn, Poland
Aleksander Lisiecki - Silesian University of Technology, Gliwice, Poland
Krzysztof Lukaszkowicz - Silesian University of Technology, Gliwice, Poland
Mariusz Łucarz - AGH University of Science and Technology, Kraków, Poland
Katarzyna Major-Gabryś - AGH University of Science and Technology, Kraków, Poland
Pavlo Maruschak - Ternopil Ivan Pului National Technical University, Ukraine
Sanjay Mohan - Shri Mata Vaishno Devi University, India
Marek Mróz - Politechnika Rzeszowska, Rzeszów, Poland
Sebastian Mróz - Czestochowa University of Technology, Poland
Kostiantyn Mykhalenkov - National Academy of Science of Ukraine, Ukraine
Dawid Myszka - Politechnika Warszawska, Warszawa, Poland
Maciej Nadolski - Czestochowa University of Technology, Częstochowa, Poland
Konstantin Nikitin - Samara State Technical University, Russia
Daniel Pakuła - Silesian University of Technology, Gliwice, Poland


This page uses 'cookies'. Learn more